Radiance temperatures at 1500 nm of niobium and molybdenum at their melting points by a pulse-heating technique

Radiance temperatures at 1500 nm of niobium and molybdenum at their melting points were measured by a pulse-heating technique. The method is based on rapid resistive self-heating of the strip-shaped specimen from room temperature to its melting point in less than 1 s and measuring the specimen radiance temperature every 0.5 ms with a high-speed infrared pyrometer. Melting of the specimen was manifested by a plateau in the radiance temperature-versus-time function. The melting-point radiance temperature for a given specimen was determined by averaging the measured values along the plateau. A total of 12 to 13 experiments was performed for each metal under investigation. The melting-point radiance temperatures for each metal were determined by averaging the results of the individual specimens. The results for radiance temperatures at 1500 nm are as follows: 1983 K for niobium and 2050 K for molybdenum. Based on the estimates of the uncertainties arising from the use of pyrometry and specimen conditions, the combined uncertainty (two standard-deviation level) in the reported Values is +/-8 K.