Synthesis and catalytic properties of perovskite-related phases in the La-Sr-Co-Cu-Ru-O system

A series of oxides of the composition La0.8Sr0.2Co1-2yCuyRuyO3 with the perovskite structure were synthesized and characterized by their X-ray diffraction (XRD) patterns and by element analysis in a transmission electron microscope (TEM) equipped with an energy-dispersive spectrometer (EDS). The XRD and TEM-EDS studies confirmed that almost monophasic samples with the perovskite structure having rhombohedral (hexagonal) symmetry were obtained for 0 less than or equal to y less than or equal to 0.20, although the simultaneous formation of a by product with the K2NiF4-type structure was observed for high y values. The lattice parameters and rhombohedral distortion increased monotonically with increasing y value due to the fact that the average ionic radius of the substituting Cu/Ru pair is larger than that of the host Co ion. Temperature-programmed desorption (TPD) studies showed that the substitution of the Cu/Ru pair for Co caused a decrease in the amount of oxygen desorbed from the bulk of the oxide, and the catalytic activity for CO oxidation and CO-NO reactions decreased. The Cu/Ru substitution did, however, selectivity increase the N-2 formation and decreased that of N2O in the GO-NO reactions. Synthesis of K2NiF4-type oxides with the overall compositions (La0.8Sr0.2)(2)Co0.50Cu0.50-xRu2O4 with z = 0.05 and 0.10 was also attempted. In both cases, tetragonal K2NiF4-type oxides having a composition close to (La0.8Sr0.2)(2)(Co,Cu)(0.97)Ru0.03O4 were obtained, implying that the solubility of Ru into the given K2NiF4-type framework is very low.