Bulk glassy Cu-based alloys with a large supercooled liquid region of 110 K

被引：23

作者：

Inoue, A ^{[1
]}

Zhang, W

机构：

[1] Tohoku Univ, Inst Mat Res, Sendai, Miyagi 9808577, Japan

[2] Japan Sci & Technol Corp, Core Res Evolut Sci & Technol, Sendai, Miyagi 9808577, Japan

来源：

APPLIED PHYSICS LETTERS | 2003年 / 83卷 / 12期

关键词：

D O I：

10.1063/1.1613813

中图分类号：

O59 [应用物理学];

学科分类号：

摘要：

The replacement of Cu by 5%Ag for Cu50Hf45Al5 glassy alloy was found to increase significantly the stability of supercooled liquid against crystallization. The supercooled liquid region reached as large as 110 K for Cu45Hf45Al5Ag5. The extension of the supercooled liquid region is due to an increase in the crystallization temperature, accompanying the change in the primary crystalline phases. The effectiveness of Ag addition was interpreted to result from the retardation of long-range atomic rearrangements for the progress of crystallization reaction. The selection of the quaternary composition enabled us to form bulk glassy alloys with diameters up to 3 mm. The Young's modulus and compressive fracture strength of the 5%Ag-containing alloy are 119 GPa and 2220 MPa, respectively. (C) 2003 American Institute of Physics.

引用

页码：2351 / 2353

页数：3

共 24 条

[1] Preparation and mechanical properties of Zr-based bulk nanocrystalline alloys containing compound and amorphous phases [J].

Fan, C ;

Takeuchi, A ;

Inoue, A .

MATERIALS TRANSACTIONS JIM, 1999, 40 (01) :42-51

[2] Anelastic behavior under tensile and shearing stresses in bulk metallic glasses [J].

Fujita, K ;

Inoue, A ;

Zhang, T ;

Nishiyama, N .

MATERIALS TRANSACTIONS, 2002, 43 (08) :1957-1960

[3] MG-CU-Y AMORPHOUS-ALLOYS WITH HIGH MECHANICAL STRENGTHS PRODUCED BY A METALLIC MOLD CASTING METHOD [J].

INOUE, A ;

KATO, A ;

ZHANG, T ;

KIM, SG ;

MASUMOTO, T .

MATERIALS TRANSACTIONS JIM, 1991, 32 (07) :609-616

[4] Stabilization of metallic supercooled liquid and bulk amorphous alloys [J].

Inoue, A .

ACTA MATERIALIA, 2000, 48 (01) :279-306

[5] NEW AMORPHOUS MG-CE-NI ALLOYS WITH HIGH-STRENGTH AND GOOD DUCTILITY [J].

INOUE, A ;

OHTERA, K ;

KITA, K ;

MASUMOTO, T .

JAPANESE JOURNAL OF APPLIED PHYSICS PART 2-LETTERS & EXPRESS LETTERS, 1988, 27 (12) :L2248-L2251

[6] AL-LA-NI AMORPHOUS-ALLOYS WITH A WIDE SUPERCOOLED LIQUID REGION [J].

INOUE, A ;

ZHANG, T ;

MASUMOTO, T .

MATERIALS TRANSACTIONS JIM, 1989, 30 (12) :965-972

[7] High strain rate superplasticity of supercooled liquid for amorphous alloys [J].

Inoue, A ;

Kawamura, Y ;

Saotome, Y .

TOWARDS INNOVATION IN SUPERPLASTICITY I, 1997, 233-2 :147-153

[8] Bulk amorphous alloys with high mechanical strength and good soft magnetic properties in Fe-TM-B (TM=IV-VIII group transition metal) system [J].

Inoue, A ;

Zhang, T ;

Takeuchi, A .

APPLIED PHYSICS LETTERS, 1997, 71 (04) :464-466

[9] Thermal stability and mechanical strength of bulk glassy Ni-Nb-Ti-Zr alloys [J].

Inoue, A ;

Zhang, W ;

Zhang, T .

MATERIALS TRANSACTIONS, 2002, 43 (08) :1952-1956

[10] Recent progress in bulk glassy alloys [J].

Inoue, A ;

Takeuchi, A .

MATERIALS TRANSACTIONS, 2002, 43 (08) :1892-1906

← 1 2 3 →