Proton insertion into ruthenium oxide film prepared by pulsed laser deposition

被引：28

作者：

Zheng, JP ^{[1
]}

Jow, TR ^{[1
]}

Jia, QX ^{[1
]}

Wu, XD ^{[1
]}

机构：

[1] LOS ALAMOS NATL LAB,SUPERCOND TECHNOL CTR,LOS ALAMOS,NM 87545

来源：

JOURNAL OF THE ELECTROCHEMICAL SOCIETY | 1996年 / 143卷 / 03期

关键词：

D O I：

10.1149/1.1836584

中图分类号：

O646 [电化学、电解、磁化学];

学科分类号：

081704 ;

摘要：

Electrochemical properties of ruthenium oxide (RuO2) films with different degrees of crystallinity were studied. The RuO2 films were grown by pulsed laser deposition at substrate temperatures from 30 to 400 degrees C. At low temperatures, the amorphous phase of RuO2 films was formed. At high temperatures, the crystalline phase of RuO2 films was obtained. From the cyclic voltammetric study in H2SO4 solution, it was found that the current response for an electrode of the amorphous RuO2 film was higher than that of the crystalline film. A proton diffusion length of larger than 5.8 nm was obtained on the RuO2 film prepared at 30 degrees C.

引用

页码：1068 / 1070

页数：3

共 13 条

[1] INNER AND OUTER ACTIVE SURFACE OF RUO2 ELECTRODES
ARDIZZONE, S
FREGONARA, G
TRASATTI, S
[J]. ELECTROCHIMICA ACTA, 1990, 35 (01) : 263 - 267
[2] CONWAY BE, 1992, P 2 INT SEM DOUBL LA
[3] JIA QX, UNPUB
[4] LITHIUM-ALUMINUM ELECTRODES AT AMBIENT-TEMPERATURES
JOW, TR
LIANG, CC
[J]. JOURNAL OF THE ELECTROCHEMICAL SOCIETY, 1982, 129 (07) : 1429 - 1434
[5] JOW TR, 1995, P MAT RES SOC S, V393
[6] KOZAWA A, 1973, EL SOC EXT ABSTR, V75, P73
[7] STUDY OF RUTHENIUM ELECTRODES BY CYCLIC VOLTAMMETRY AND X-RAY-EMISSION SPECTROSCOPY
MICHELL, D
RAND, DAJ
WOODS, R
[J]. JOURNAL OF ELECTROANALYTICAL CHEMISTRY, 1978, 89 (01) : 11 - 27
[8] Raistrick I.D., 1992, ELECTROCHEMISTRY SEM, P297
[9] Trasatti S., 1980, ELECTRODES CONDUCT A, P301
[10] ZAGHIB K, 1995, RECHARGEABLE LITHIUM, P121

← 1 2 →