Filamentary and tubular silicon carbide nanocrystals

被引:2
作者
Lutsenko, VG [1 ]
机构
[1] Natl Acad Sci Ukraine, Inst Gen & Inorgan Chem, Kiev, Ukraine
关键词
silicon carbide; nanotube; nanofilament; whisker;
D O I
10.1007/s11106-005-0049-7
中图分类号
TQ174 [陶瓷工业]; TB3 [工程材料学];
学科分类号
0805 ; 080502 ;
摘要
Filamentary crystals and nanotubes of 3C-SiC containing, alpha-SiC are prepared. The nanostructures of SiC are synthesized from a mixture of hydrocarbons, chlorosilane and hydrogen in the presence of iron (Fe(CO)(5)) at 1250 degrees C. The average nanofilament diameter is 30 nm. The nanotube diameter ranges from 10 to 200 nm.
引用
收藏
页码:1 / 4
页数:4
相关论文
共 15 条
[1]  
BELETSKII VM, 1990, MOSC INT C COMP, V1, P184
[2]  
BELETSKII VM, 1986, POROSHKOV METALL, P44
[3]  
EAST WR, 1988, MATER ENG, V105, P33
[4]  
GADKAREE KP, 1986, AM CERAM SOC B, V65, P372
[5]  
Givargizov E. I., 1977, GROWTH FILAMENTARY L
[6]  
GRIBKOV VN, 1983, 2 ALL UN C COMP POLY, V1, P66
[7]   FRACTURE-TOUGHNESS ANISOTROPY AND TOUGHENING MECHANISMS OF A HOT-PRESSED ALUMINA REINFORCED WITH SILICON-CARBIDE WHISKERS [J].
HANSSON, T ;
WARREN, R ;
WASEN, J .
JOURNAL OF THE AMERICAN CERAMIC SOCIETY, 1993, 76 (04) :841-848
[8]   Synthesis and characterization of SiC nanowires through a reduction-carburization route [J].
Hu, JQ ;
Lu, QK ;
Tang, KB ;
Deng, B ;
Jiang, RR ;
Qian, YT ;
Yu, WC ;
Zhou, GE ;
Liu, XM ;
Wu, JX .
JOURNAL OF PHYSICAL CHEMISTRY B, 2000, 104 (22) :5251-5254
[9]  
Kharlamov A.I., 2002, THEOR EXP CHEM, V38, P232
[10]  
LUTSENKO VG, 1993, POROSHKOV METALL, P80