Effect of phosphorus on activity of hydrotreating catalyst of Maya heavy crude

The effect of phosphorus on physical properties of the catalyst and on activity of hydrotreating of Maya crude was studied in this work. Catalysts were prepared by the co-impregnation method. Alumina-titania binary oxide was used as a support material. The presence of phosphorus in the catalyst decreases the percentage of micropores, and it results in a decrease of specific surface area. Temperature program reduction (TPR) shows that phosphates reduce metal support interaction. It leads to the formation of polymolybdate phases in expense of strongly bonded tetrahedral molybdates. At higher P loading, polymolybdates may be present with quasi crystalline MoO3. However, the TPR experiment is not sufficiently sensitive to distinguish several phases present on the catalysts used by the authors. A slight increment of HDM activity is observed, but HDS activity is lower in the P containing catalyst compared with the P free catalyst. The changes of physical properties of the spent catalysts are mainly due to the coke formation on the catalyst. The presence of phosphor-us on hydrotreating catalysts inhibits coke formation during the hydrotreating reaction. (c) 2005 Elsevier B.V. All rights reserved.