Preparation of polymeric porous materials by interparticle crosslinking

被引：13

作者：

Dauben, M

Reichert, KH

Huang, PC

Fock, J

机构：

[1] BEIJING INST TECHNOL,DEPT CHEM ENGN,BEIJING 100081,PEOPLES R CHINA

[2] TH GOLDSCHMIDT AG,D-45127 ESSEN,GERMANY

来源：

POLYMER | 1996年 / 37卷 / 13期

关键词：

porous polymeric materials; interparticle crosslinking; poly(acrylic acid);

D O I：

10.1016/0032-3861(96)87647-6

中图分类号：

O63 [高分子化学（高聚物）];

学科分类号：

070305 ; 080501 ; 081704 ;

摘要：

Suspensions of poly(acrylic acid) particles with an average diameter of about 90 nm in benzene were prepared by dispersion polymerization. Using dioyl dichloride or diglycidyl ether as crosslinking agent the poly(acrylic acid) particles can be linked with each other, and a gel with three-dimensional network structure was formed. After removal of the solvent from the gel by freeze-drying a porous polymeric material can be obtained. Depending on the concentration of crosslinking agent and the polymer content of the suspension a porous material of poly(acrylic acid) with porosity as high as 0.95 and density as low as 0.07 g cm(-3) is achieved. The process of gelation was studied by dynamic rheology, light scattering and calorimetric measurements. Copyright (C) 1996 Elsevier Science Ltd.

引用

页码：2827 / 2830

页数：4

共 8 条

[1]

DULLIEN FAL, 1979, POROUS MEDIA FLUID T, P77

[2] KINETICS AND PARTICLE FORMATION IN THE PRECIPITATION POLYMERIZATION OF ACRYLIC-ACID IN THE PRESENCE OF POLYSTYRENE-BLOCK-POLY(ETHYLENE OXIDE) COPOLYMERS [J].