Calcium phosphate bioceramics research in Latvia

被引:14
作者
Gross, KA
Berzina, L
Cimdins, R
Gross, V
机构
[1] Riga Tech Univ, Dept Silicate Technol, Biomat Res & Dev Lab, LV-1048 Riga, Latvia
[2] CSIRO, Div Mat Sci & Technol, Clayton, Vic 3168, Australia
关键词
D O I
10.1016/S0272-8842(98)00028-5
中图分类号
TQ174 [陶瓷工业]; TB3 [工程材料学];
学科分类号
0805 ; 080502 ;
摘要
Calcium phosphate bioceramics including glass-ceramics and hydroxyapatite have been manufactured and investigated for implantation purposes. Three glass systems were selected based on CaO and P2O5 and an inert metal oxide (either Ta2O5, TiO2 or Nb2O5). Different compositions were found giving crystal phases in a glassy matrix. These glass-ceramics were tested for strength with 4-point bending, and the biocompatibility ascertained using in vitro and in vivo tests. The Nb2O5 containing glass-ceramic showed bone apposition and was found to be a suitable material for implantation. Hydroxyapatite was produced using the wet method and it was found that the pH during the reaction and the dispersivity of the Ca(OH)(2) influence the purity of the powder. The pH was controlled by addition of ammonium hydroxide to the precipitate. Hydroxyapatite sprayed onto grit blasted titanium showed low strengths of 20-30 MPa with adhesive failure but was increased to 60-70 MPa with an intermediate glass layer. Composites of glass-ceramic with hydroxyapatite exhibited a higher strength than hydroxyapatite with a value of 100-120 MPa. (C) 1999 Elsevier Science Limited and Techna S.r.l. All rights reserved.
引用
收藏
页码:231 / 237
页数:7
相关论文
共 23 条
  • [1] A CALCIUM HYDROXYAPATITE PRECIPITATED FROM AN AQUEOUS-SOLUTION - AN INTERNATIONAL MULTIMETHOD ANALYSIS
    ARENDS, J
    CHRISTOFFERSEN, J
    CHRISTOFFERSEN, MR
    ECKERT, H
    FOWLER, BO
    HEUGHEBAERT, JC
    NANCOLLAS, GH
    YESINOWSKI, JP
    ZAWACKI, SJ
    [J]. JOURNAL OF CRYSTAL GROWTH, 1987, 84 (03) : 515 - 532
  • [2] BERZINA L, 1995, EUROCERAMICS, P85
  • [3] BERZINA L, 1989, THESIS RIGA TU LATVI
  • [4] BERZINA L, 1994, BIOCERAMICS, V7, P151
  • [5] BIOMATERIALS IN ORTHOPEDIC SURGERY
    COHEN, J
    [J]. AMERICAN JOURNAL OF SURGERY, 1967, 114 (01) : 31 - &
  • [6] Gross KA, 1997, INT J ORAL MAX IMPL, V12, P589
  • [7] ALUMINA CERAMIC, A NEW BIOMATERIAL - PROPERTIES OF MATERIALS AND POSSIBLE AREAS OF CLINICAL APPLICATION
    HEIMKE, G
    GRISS, P
    ANDRIANW.HF
    KREMPIEN, B
    [J]. ARCHIVES OF ORTHOPAEDIC AND TRAUMA SURGERY, 1974, 78 (03) : 216 - 226
  • [8] Hench L L, 1973, Med Instrum, V7, P136
  • [9] BIOMATERIALS
    HENCH, LL
    [J]. SCIENCE, 1980, 208 (4446) : 826 - 831
  • [10] HULBERT S F, 1970, Journal of Biomedical Materials Research, V4, P433, DOI 10.1002/jbm.820040309