Conducting film from graphite oxide nanoplatelets and poly(acrylic acid) by layer-by-layer self-assembly

被引：87

作者：

Wu, Jihuai ^{[1
]}

Tang, Qunwei ^{[1
]}

Sun, Hui ^{[1
]}

Lin, Jianming ^{[1
]}

Ao, Haiyong ^{[1
]}

Huang, Miaoliang ^{[1
]}

Huang, Yunfang ^{[1
]}

机构：

[1] Huaqiao Univ, Inst Mat Phys Chem, Key Lab Funct Mat Fujian Higher Educ, Quanzhou 362021, Peoples R China

来源：

LANGMUIR | 2008年 / 24卷 / 09期

关键词：

D O I：

10.1021/la800095z

中图分类号：

O6 [化学];

学科分类号：

0703 ;

摘要：

A [poly(acrylicacid)/graphite oxide](n) [(PAA/GO)(n)] film with a conductivity of 60S.cm(-1) was grown layer-by-layer (LbL) using Langmuir-Blodgett self-assembly techniques. GO nanoplatelets were prepared from natural graphite by oxidizing, ball milling, exfoliating, and modifying with cationic surfactant cetyltrimethyl ammonium bromide (CTAB). The X-ray diffraction pattern reveals that PAA and GO stack orderly LbL and repeatedly in the (PAA/GO),, films, and about three carbon molecular layers are superposed on each GO sheet. Fourier transform infrared spectra offer evidence for the interaction between the carboxylic groups on PAA and the CTAB on the surface of the GO nanoplatelets. Electrochemistry measurements show that the conductivity of the (PAA/GO), film depends on the carbon-carbon interlayer height of the GO sheet, and the (PAA/GO), film has a typical positive temperature coefficient effect above the PAA melting temperature. The atomic force microscopy images reveal that CTAB molecules stack in a wellordered head-to-head structure on both surfaces of the GO nanoplatelets and the GO nanoplatelets are embeded between PAA layers.

引用

页码：4800 / 4805

页数：6

共 43 条

[1] Surfactant aggregation at a hydrophobic surface [J].