Subsolidus phase equilibria in the NiO-CeO2 and La2O3-CeO2-Fe2O3 systems

被引:48
作者
Hrovat, M [1 ]
Holc, J [1 ]
Bernik, S [1 ]
Makovec, D [1 ]
机构
[1] Jozef Stefan Inst, Ljubljana 1001, Slovenia
关键词
oxides; electron microscopy; X-ray diffraction; phase equilibria;
D O I
10.1016/S0025-5408(98)00103-2
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
Subsolidus equilibria in air in the NiO-CeO2 and La2O3-CeO2-Fe2O3 systems were studied. In the NiO-CeO2 and Fe2O3-CeO2 systems, no binary compound and no solid solubility were detected. La2O3 was soluble in CeO2, forming a cubic fluorite solid solution up to La0.5Ce0.5O1.75, whereas no solid solubility of CeO2 in La2O3 was detected. In the La2O3-CeO2-Fe2O3 system, no ternary compound was found. The tie line is between LaFeO3 and CeO2. (C) 1998 Elsevier Science Ltd.
引用
收藏
页码:1175 / 1183
页数:9
相关论文
共 21 条
[1]   BISMUTH OXIDE-BASED SOLID ELECTROLYTES FOR FUEL-CELLS [J].
AZAD, AM ;
LAROSE, S ;
AKBAR, SA .
JOURNAL OF MATERIALS SCIENCE, 1994, 29 (16) :4135-4151
[2]  
BELOV BF, 1983, INORG MATER+, V19, P231
[3]   IMMITTANCE RESPONSE OF LA0.6SR0.4CO0.2FE0.8O3 BASED ELECTROCHEMICAL-CELLS [J].
CHEN, CC ;
NASRALLAH, MM ;
ANDERSON, HU .
JOURNAL OF THE ELECTROCHEMICAL SOCIETY, 1995, 142 (02) :491-496
[4]   PREPARATION AND PROPERTIES OF SOME PHASES IN THE SYSTEM ND2O3-CEO2-ZRO2-RUO2 [J].
DIXON, S ;
MARR, J ;
LACHOWSKI, EE ;
GARD, JA ;
GLASSER, FP .
MATERIALS RESEARCH BULLETIN, 1980, 15 (12) :1811-1816
[5]  
Eguchi K., 1995, Proceedings of the Fourth International Symposium on Solid Oxide Fuel Cells (SOFC-IV), P676
[6]  
Godickemeier M., 1995, Proceedings of the Fourth International Symposium on Solid Oxide Fuel Cells (SOFC-IV), P1072
[7]   CRYSTALLOGRAPHIC, THERMAL AND ELECTROCHEMICAL PROPERTIES OF THE SYSTEM LA1-XSRXMNO3 FOR HIGH-TEMPERATURE SOLID ELECTROLYTE FUEL-CELLS [J].
HAMMOUCHE, A ;
SIEBERT, E ;
HAMMOU, A .
MATERIALS RESEARCH BULLETIN, 1989, 24 (03) :367-380
[8]  
Jerdal L. O., 1995, Proceedings of the Fourth International Symposium on Solid Oxide Fuel Cells (SOFC-IV), P544
[9]   FUEL-CELLS - ENERGY-CONVERSION FOR THE NEXT CENTURY [J].
KARTHA, S ;
GRIMES, P .
PHYSICS TODAY, 1994, 47 (11) :54-61
[10]   OXIDATION REDUCTION BEHAVIOR OF UNDOPED AND SR-DOPED LAMNO3 - DEFECT STRUCTURE, ELECTRICAL-CONDUCTIVITY, AND THERMOELECTRIC-POWER [J].
KUO, JH ;
ANDERSON, HU ;
SPARLIN, DM .
JOURNAL OF SOLID STATE CHEMISTRY, 1990, 87 (01) :55-63