Electrophoretic deposition and compression of titania nanoparticle films for dye-sensitized solar cells

Cathodic electrophoretic deposition (EPD) of commercially available TiO2 nanocrystals (P-25 and P-90, Degussa) for the formation of nanoporous electrodes for dye-sensitized solar cells (DSSCs) is reported. Thick, uniform, adherent TiO2 films were obtained from alcoholic suspensions prepared in two steps: first, nanoparticles were treated in an alcoholic suspension with a small amount of acetylacetone: second, the obtained suspension was mixed with a EPD "charging solution" with small additives of iodine, acetone and water. A modified mechanical compression technique was employed to the electrophoretically deposited films to vary the porous structure and thickness of TiO2 layers. By applying non-polar volatile organic liquids to fill the pores of dry TiO2 films before compression, we obtained a substantial improvement in the quality of the pressed films. The fabrication of multilayer electrodes enabled us to obtain TiO2 films with a thickness up to 25 mu m and the photoelectric conversion efficiency up to 8.5% under 1 sun illumination. (c) 2008 Elsevier B.V. All rights reserved.