Mesoporous TiO2-based photocatalysts for UV and visible light gas-phase toluene degradation

被引:79
作者
Bosc, F
Edwards, D
Keller, N
Keller, V
Ayral, A
机构
[1] Univ Strasbourg 1, UMR 7515, CNRS, ECPM,Lab Mat Surfaces & Procedes Catalyse, F-67087 Strasbourg, France
[2] ELCASS, European Lab Catalysis & Surface Sci, F-67087 Strasbourg, France
[3] Univ Montpellier 2, Inst Europeen Membranes, UMR 5635, CNRS,ENSCM, F-34095 Montpellier, France
关键词
mesoporous TiO2 anatase; hexagonal and cubic structure; toluene; coupled semiconductors; photogenerated charge recombination; confinement effect;
D O I
10.1016/j.tsf.2005.08.361
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
UV and visible light photocatalytic removal of concentrated toluene (110 ppm) in the gas phase was performed in an annular flow-reactor on mesoporous anatase TiO2 supported WO3 photocatalysts. Depending on the template, hexagonal and cubic mesoporous TiO2 thin layers were obtained by dip-coating of an anatase sol onto slides of soda lime-silica glass, which was then mechanically removed. The coupling of low contents of WO3 (4 wt.%) with mesoporous anatase TiO2 led to high photocatalytic efficiency both using UV and visible light activation. The highly positive effect of WO3 on the toluene removal efficiency was attributed to a one-way and a two-way coupling phenomena depending on the photocatalyst nature and on the activation source. The hypothesis of a confinement effect of the reactants inside the mesoporous structure, based on an increase in their partial pressure on the active sites, was put forward to explain the high photocatalytic performances obtained under UV and visible light activation. (c) 2005 Published by Elsevier B.V.
引用
收藏
页码:272 / 279
页数:8
相关论文
共 44 条
[1]   General predictive syntheses of cubic, hexagonal, and lamellar silica and titania mesostructured thin films [J].
Alberius, PCA ;
Frindell, KL ;
Hayward, RC ;
Kramer, EJ ;
Stucky, GD ;
Chmelka, BF .
CHEMISTRY OF MATERIALS, 2002, 14 (08) :3284-3294
[2]  
[Anonymous], 1989, PHOTOCATALYSIS FUNDA
[3]   Visible-light photocatalysis in nitrogen-doped titanium oxides [J].
Asahi, R ;
Morikawa, T ;
Ohwaki, T ;
Aoki, K ;
Taga, Y .
SCIENCE, 2001, 293 (5528) :269-271
[4]   Photocatalytic oxidation of gaseous toluene on anatase TiO2 catalyst:: mechanistic aspects and FT-IR investigation [J].
Augugliaro, V ;
Coluccia, S ;
Loddo, V ;
Marchese, L ;
Martra, G ;
Palmisano, L ;
Schiavello, M .
APPLIED CATALYSIS B-ENVIRONMENTAL, 1999, 20 (01) :15-27
[5]  
BAHNEMANN D, 1999, ENV PHOTOCHEMISTRY, V2, P285
[6]   Sulfate-promoted titania photocatalyst for high efficiency gas phase toluene degradation [J].
Barraud, E ;
Bosc, F ;
Keller, N ;
Keller, V .
CHEMISTRY LETTERS, 2005, 34 (03) :336-337
[7]   Cubic mesoporous frameworks with a mixed semiconductor nanocrystalline wall structure and enhanced sensitivity to visible light [J].
Bartl, MH ;
Puls, SP ;
Tang, J ;
Lichtenegger, HC ;
Stucky, GD .
ANGEWANDTE CHEMIE-INTERNATIONAL EDITION, 2004, 43 (23) :3037-3040
[8]   Mesostructure of anatase thin films prepared by mesophase templating [J].
Bosc, F ;
Ayral, A ;
Albouy, PA ;
Datas, L ;
Guizard, C .
CHEMISTRY OF MATERIALS, 2004, 16 (11) :2208-2214
[9]   A simple route for low-temperature synthesis of mesoporous and nanocrystalline anatase thin films [J].
Bosc, F ;
Ayral, A ;
Albouy, PA ;
Guizard, C .
CHEMISTRY OF MATERIALS, 2003, 15 (12) :2463-2468
[10]  
Bosc F., 2004, THESIS U MONTPELLIER