Sliding wear behaviour of ion implanted ultra high molecular weight polyethylene against a surface modified titanium alloy Ti-6Al-4V

A study has been made of the sliding wear behaviour of untreated and ion implanted ultra high molecular weight polyethylene (UHMWPE) against a surface modified titanium alloy (Ti-6Al-4V) using a pin on disc apparatus. It was found that the presence of water lubrication and a very smooth counterface was necessary to maintain low wear rates of the UHMWPE. A 'zero wear' effect was observed when nitrogen implanted UHMWPE was tested against very smooth counterfaces (R(a) approximate to 0.03 mu m) of either surface oxidized or nitrogen implanted Ti-6Al-4V under water lubrication. The enhanced mechanical and physical properties of the surface treated materials are believed to be responsible for the improved wear performance. Copyright (C) 1996 Elsevier Science Ltd