Estimation of the physical wood properties of green Pinus taeda radial samples by near infrared spectroscopy

The application of near infrared (NIR) spectroscopy to the green wood of radial samples (simulated increment cores) and the development of calibrations for the prediction of wood properties are described. Twenty Pinus taeda L. (loblolly pine) radial strips were characterized in terms of air-dry density, microfibril angle (MFA), and stiffness. NIR spectra were obtained in 10-mm steps from the radial longitudinal and transverse faces of each sample and used to develop calibrations for each property. NIR spectra were collected when the wood was green (moisture content ranged from approximately 100% to 154%) and dried to approximately 7% moisture content. Relationships between measured and NIR estimates for green wood were good; coefficients of determination (R-2) ranged from 0.79 (MFA) to 0.85 (air-dry density). Differences between calibrations developed using the radial longitudinal and transverse faces were small. Calibrations were tested on an independent set. Predictive errors were relatively large for some green samples and relationships were moderate; R-p(2) ranged from 0.67 (MFA) to 0.81 (stiffness). Dry wood calibrations demonstrated strong predictive relationships with R-p(2) ranging from 0.87 (air-dry density) to 0.95 (stiffness). NIR spectroscopy has the potential to predict the air-dry density, MFA, and stiffness of 10-mm sections of green P. taeda wood samples.