Electrical and electromagnetic interference shielding properties of flow-induced oriented carbon nanotubes in polycarbonate

被引：343

作者：

Arjmand, Mohammad ^{[1
]}

Mahmoodi, Mehdi ^{[2
]}

Gelves, Genaro A. ^{[1
]}

Park, Simon ^{[2
]}

Sundararaj, Uttandaraman ^{[1
]}

机构：

[1] Univ Calgary, Dept Chem & Petr Engn, Calgary, AB T2N 1N4, Canada

[2] Univ Calgary, Dept Mech & Mfg Engn, Calgary, AB T2N 1N4, Canada

来源：

CARBON | 2011年 / 49卷 / 11期

基金：

加拿大自然科学与工程研究理事会;

关键词：

FIBER ORIENTATION; POLYMER MATRIX; COMPOSITES; CONDUCTION; ALIGNMENT; BLENDS;

D O I：

10.1016/j.carbon.2011.04.039

中图分类号：

O64 [物理化学（理论化学）、化学物理学];

学科分类号：

070304 ; 081704 ;

摘要：

The electrical and electromagnetic interference shielding effectiveness (EMI SE) properties of multi-walled carbon nanotubes/polycarbonate (MWCNT/PC) composites are investigated. The composites were prepared by diluting masterbatch (15 wt.% MWCNT) using a Haake mixer and then injection-molded into a dog-bone mold. Various MWCNT alignments were created by changing operating conditions. Electrical resistivity measurements were carried out at three different areas at both parallel and perpendicular to the flow direction. The results showed higher resistivity and percolation threshold at higher alignments in both parallel and perpendicular to the flow direction. By applying Ohm's law it was seen that after percolation, the field emission mechanisms are more important at higher orientations. Higher MWCNT alignments were observed in areas with higher resistivities, and this was verified using SEM, TEM and Raman spectroscopy techniques. Additionally, EMI SE measurements were done on compression-molded samples at different concentrations and thicknesses. The results showed that both EMI SE by reflection and absorption increased with increase in MWCNT loading and shielding material thickness. (C) 2011 Elsevier Ltd. All rights reserved.

引用

页码：3430 / 3440

页数：11

共 48 条

[1] Flow induced orientation of multiwalled carbon nanotubes in polycarbonate nanocomposites: Rheology, conductivity and mechanical properties [J].

Abbasi, Samaneh ;

Carreau, Pierre J. ;

Derdouri, Abdessalem .

POLYMER, 2010, 51 (04) :922-935

[2] Electromagnetic interference (EMI) shielding effectiveness of PP/PS polymer blends containing high structure carbon black [J].

Al-Saleh, Mohammed H. ;

Sundararaj, Uttandaraman .

MACROMOLECULAR MATERIALS AND ENGINEERING, 2008, 293 (07) :621-630

[3] Electromagnetic interference shielding mechanisms of CNT/polymer composites [J].

Al-Saleh, Mohammed H. ;

Sundararaj, Uttandaraman .

CARBON, 2009, 47 (07) :1738-1746

[4]

ALSALEH MH, 2008, THESIS U ALBERTA EDM

[5] TUNNELING AND NONUNIVERSAL CONDUCTIVITY IN COMPOSITE-MATERIALS [J].

BALBERG, I .

PHYSICAL REVIEW LETTERS, 1987, 59 (12) :1305-1308

[6] A review and analysis of electrical percolation in carbon nanotube polymer composites [J].

Bauhofer, Wolfgang ;

Kovacs, Josef Z. .

COMPOSITES SCIENCE AND TECHNOLOGY, 2009, 69 (10) :1486-1498

[7]

Beek V., 1964, Carbon, V2, P121

[8]

BEEK V, 1962, J APPL POLYM SCI, V6, P651

[9] Effects of nanotube alignment and measurement direction on percolation resistivity in single-walled carbon nanotube films [J].

Behnam, Ashkan ;

Guo, Jing ;

Ural, Ant .

JOURNAL OF APPLIED PHYSICS, 2007, 102 (04)

[10]

Blythe A.R., 2005, Electric Properties of Polymers

← 1 2 3 4 5 →