Yttrium-promoted selective oxidation of aluminium in the oxidation at 1100°C of an eutectic Ni-Al-Cr3C2 alloy

被引:20
作者
Castello, P
Stott, FH
Gesmundo, F
机构
[1] Univ Genoa, Fac Ingn, Ist Chim, I-16129 Genoa, Italy
[2] Univ Manchester, Inst Sci & Technol, Ctr Corros & Protect, Manchester M60 1QD, Lancs, England
关键词
oxidation; directionally-solidified alloys; multiphase alloys; reactive-element effect;
D O I
10.1016/S0010-938X(98)00162-0
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
The effects of an yttrium addition of 0.2 wt% on the oxidation behaviour of an eutectic Ni-Al-Cr3C2 alloy of average composition Ni-12.3 Cr-6.9 Al-1.8 C (wt%) have been investigated at 1100 degrees C in 1 atm oxygen. Experiments have been carried out under isothermal and thermal cycling conditions on the as-cast alloy, in which Cr,C, was present as a finely dispersed eutectic phase, and on directionally-solidified specimens having an aligned structure, In all cases, Al2O3 formed almost entirely as an external scale. Although Cr2O3 formed in some regions of the surface in the early stages, compact subsurface Al2O3 layers generally developed beneath such locations, protecting the alloy from severe internal attack. This behaviour is quite different from that observed for similar yttrium-free alloys, where aluminium was oxidized internally beneath continuous external Cr2O3 scales. In the present case, while it was almost certainly formed during the transient stage, the growth rate of Cr2O3 was probably reduced due to the presence of the reactive element and the extent of chromium depletion in the alloy was thereby decreased. This yielded an increase in the concentration of chromium in the alloy at its interface with the transient Cr2O3 scale compared to the yttrium-free alloy, with a corresponding decrease in the oxygen activity at the same location. As a consequence, the inward flux of oxygen in the alloy was reduced, allowing a transition from internal to external oxidation of aluminium to become possible on longer periods of oxidation, The presence of carbides at the alloy/scale interface was highly detrimental to the adhesion of the oxide scale to the metal substrate, and the scales tended to crack and/or lift on cooling. However, no massive spalling occurred, even during thermal cycling for periods up to 124 h, while the Al2O3 scales tended to re-form rapidly after mechanical damage. (C) 1999 Elsevier Science Ltd. All rights reserved.
引用
收藏
页码:901 / 918
页数:18
相关论文
共 32 条
  • [1] DOPANT EFFECT OF YTTRIUM AND THE GROWTH AND ADHERENCE OF ALUMINA ON NICKEL-ALUMINUM ALLOYS
    ANDERSON, AB
    MEHANDRU, SP
    SMIALEK, JL
    [J]. JOURNAL OF THE ELECTROCHEMICAL SOCIETY, 1985, 132 (07) : 1695 - 1701
  • [2] The oxidation of a directionally solidified Ni-Al-Cr3C2 alloy at 1100 and 1200°C in oxygen
    Castello, P
    Stott, FH
    Gesmundo, F
    [J]. OXIDATION OF METALS, 1998, 49 (5-6): : 583 - 610
  • [3] THE INFLUENCE OF IMPLANTED YTTRIUM ON THE MECHANISM OF GROWTH OF CR2O3 ON CR
    COTELL, CM
    YUREK, GJ
    HUSSEY, RJ
    MITCHELL, DF
    GRAHAM, MJ
    [J]. JOURNAL OF THE ELECTROCHEMICAL SOCIETY, 1987, 134 (07) : 1871 - 1872
  • [4] COTELL CM, 1990, OXID MET, V34, P173, DOI 10.1007/BF00665014
  • [5] THE INFLUENCE OF GRAIN-BOUNDARY SEGREGATION OF Y IN CR2O3 ON THE OXIDATION OF CR METAL .2. EFFECTS OF TEMPERATURE AND DOPANT CONCENTRATION
    COTELL, CM
    YUREK, GJ
    HUSSEY, RJ
    MITCHELL, DF
    GRAHAM, MJ
    [J]. OXIDATION OF METALS, 1990, 34 (3-4): : 201 - 216
  • [6] FUNKENBUSH AW, 1985, MET T A, V17, P1164
  • [7] The steady-state corrosion kinetics of two-phase binary alloys forming the most-stable oxide
    Gesmundo, F
    Castello, P
    Viani, F
    [J]. OXIDATION OF METALS, 1996, 46 (5-6): : 383 - 398
  • [8] OXIDATION OF NI-CR-AL ALLOYS BETWEEN 1000 DEGREES AND 1200 DEGREES C
    GIGGINS, CS
    PETTIT, FS
    [J]. JOURNAL OF THE ELECTROCHEMICAL SOCIETY, 1971, 118 (11) : 1782 - &
  • [9] INFLUENCE OF YTTRIUM ADDITIONS ON OXIDE-SCALE ADHESION TO AN IRON-CHROMIUM-ALUMINUM ALLOY
    GOLIGHTLY, FA
    STOTT, FH
    WOOD, GC
    [J]. OXIDATION OF METALS, 1976, 10 (03): : 163 - 187
  • [10] OXIDATION AND INTERGRANULAR DISINTEGRATION OF THE ALUMINIDES NIAL AND NBAL3 AND PHASES IN THE SYSTEM NB-NI-AL
    GRABKE, HJ
    STEINHORST, M
    BRUMM, M
    WIEMER, D
    [J]. OXIDATION OF METALS, 1991, 35 (3-4): : 199 - 222