High temperature oxidation behaviour of directionally solidified nickel base superalloy CM-247LC

被引:40
作者
Das, DK [1 ]
Singh, V
Joshi, SV
机构
[1] Def Met Res Lab, Hyderabad 500058, Andhra Pradesh, India
[2] Banaras Hindu Univ, Dept Engn Met, Varanasi 221005, Uttar Pradesh, India
[3] Int Adv Res Ctr Powder Met & New Mat, Hyderabad 500005, Andhra Pradesh, India
关键词
D O I
10.1179/026708303225001975
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
The present paper describes the isothermal and cyclic oxidation behaviour of the technologically important nickel base directionally solidified superalloy CM - 247LC in air in the temperature range 1000 - 1200degreesC. This superalloy behaves as a transition nickel base alloy under isothermal oxidation conditions and exhibits a fairly long transient oxidation period (similar to20 h at 1100degreesC). Irrespective of the temperature of exposure and nature of oxidation (isothermal or cyclic), a composite oxide scale develops on CM - 247LC. While the outer portion of the oxide scale consists of either spinel (NiAl2O4) or a mixture of spinel and NiO, depending on oxidation temperature, the inner portion is always constituted of alumina. Beyond the transient period, the alloy is found to follow parabolic oxidation kinetics. The oxide layer that forms is invariably very non-uniform in thickness, and is dispersed with two types of oxide particles. While tantalum rich oxide particles are found scattered in the outer zone of the oxide layer, hafnium rich oxide particles lie close to the oxide/metal interface. Results also reveal that the nature of oxidation associated with the CM - 247LC superalloy causes entrapment of metal islands in the oxide layer.
引用
收藏
页码:695 / 708
页数:14
相关论文
共 18 条
[1]  
ANGENETE J, 2002, THESIS U TECHNOLOGY
[2]   MICROSTRUCTURE OF OXIDE SCALES FORMED ON CYCLICALLY OXIDIZED M-CR-AL-Y COATINGS [J].
CHOQUET, P ;
INDRIGO, C ;
MEVREL, R .
MATERIALS SCIENCE AND ENGINEERING, 1987, 88 :97-101
[3]   Evolution of aluminide coating microstructure on nickel-base cast superalloy CM-247 in a single-step high-activity aluminizing process [J].
Das, DK ;
Singh, V ;
Joshi, SV .
METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1998, 29 (08) :2173-2188
[4]  
DEBOER GJ, 1981, CR167992, V1, P17
[5]  
Erickson G. L., 1985, P GAS TURB C EXH HOU
[6]  
ERICKSON GL, 1983, 004 CANN MUSK INT
[7]   OXIDE ADHESION AND GROWTH-CHARACTERISTICS ON PLATINUM-MODIFIED ALUMINIDE COATINGS [J].
FARRELL, MS ;
BOONE, DH ;
STREIFF, R .
SURFACE & COATINGS TECHNOLOGY, 1987, 32 (1-4) :69-84
[8]   OXIDATION OF NI-CR-AL ALLOYS BETWEEN 1000 DEGREES AND 1200 DEGREES C [J].
GIGGINS, CS ;
PETTIT, FS .
JOURNAL OF THE ELECTROCHEMICAL SOCIETY, 1971, 118 (11) :1782-&
[9]   IMPROVEMENT OF THE OXIDATION RESISTANCE OF SUPERALLOYS BY LOW-PRESSURE, PLASMA-SPRAYED MCRALYTA COATINGS .1. [J].
HUNTZ, AM ;
BOUMAZA, A ;
MOULIN, G .
OXIDATION OF METALS, 1988, 30 (3-4) :141-183
[10]  
JEDLINSKI J, 1988, MAT SCI ENG A-STRUCT, V121, P539