Preparation and characterization of self-assembled polyelectrolyte multilayered films on electrospun nanofibers

被引：44

作者：

Ding, B ^{[1
]}

Fujimoto, K

Shiratori, S

机构：

[1] Keio Univ, Grad Sch Sci & Technol, Yokohama, Kanagawa 2238522, Japan

[2] SNT Co Ltd, Kawasaki, Kanagawa 2120054, Japan

来源：

THIN SOLID FILMS | 2005年 / 491卷 / 1-2期

关键词：

thin films; electrospun nanofibers; fourier transform infrared spectroscopy (FTIR); surface morphology;

D O I：

10.1016/j.tsf.2005.02.009

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

Self-assembled polyelectrolyte multilayered (PEM) films were fabricated on electrospun cellulose acetate (CA) nanofibers via the electrostatic layer-by-layer adsorption of oppositely charged poly(allylamine hydrochloride) (PAH) and poly(acrylic acid) (PAA). The growth of PEM films on CA nanofibers was studied by regulating the pH value of polyelectrolyte, solutions and the number of PAH/PAA bilayers. The composition and morphology of PEM films coated fibrous mats were examined by Fourier transform infrared spectroscopy, field emission scanning electron microscopy, and atomic force microscopy. The results indicated that the growth of PEM films fabricated at a PAH pH of 7.5 and a PAA pH of 3.5 (PAH7.5/PAA3.5) was much quicker than that of films of PAH and PAA adsorbed at pH 5 (PAH5/PAA5). The CA nanofibers were embedded in the thick PAH7.5/PAA3.5 films. The average diameter of PAH5/PAA5 films coated fibers and average PAH5/PAA5 film thickness gradually increased with increasing the number of PEM bilayers. Moreover, the surface roughness of fibers was increased after deposition of PAH/PAA films. (c) 2005 Elsevier B.V. All rights reserved.

引用

页码：23 / 28

页数：6

共 32 条

[1]

Caruso F, 2001, ADV MATER, V13, P11, DOI 10.1002/1521-4095(200101)13:1<11::AID-ADMA11>3.0.CO

[2]

2-N

[3] Nanoengineering of inorganic and hybrid hollow spheres by colloidal templating [J].

Caruso, F ;

Caruso, RA ;

Möhwald, H .

SCIENCE, 1998, 282 (5391) :1111-1114

[4] Preparation of nanoparticle coatings on surfaces of complex geometry [J].

Crisp, MT ;

Kotov, NA .

NANO LETTERS, 2003, 3 (02) :173-177

[5] Fuzzy nanoassemblies: Toward layered polymeric multicomposites [J].

Decher, G .

SCIENCE, 1997, 277 (5330) :1232-1237

[6] BUILDUP OF ULTRATHIN MULTILAYER FILMS BY A SELF-ASSEMBLY PROCESS .1. CONSECUTIVE ADSORPTION OF ANIONIC AND CATIONIC BIPOLAR AMPHIPHILES ON CHARGED SURFACES [J].

DECHER, G ;

HONG, JD .

MAKROMOLEKULARE CHEMIE-MACROMOLECULAR SYMPOSIA, 1991, 46 :321-327

[7] Fabrication of blend biodegradable nanofibrous nonwoven mats via multi-jet electrospinning [J].

Ding, B ;

Kimura, E ;

Sato, T ;

Fujita, S ;

Shiratori, S .

POLYMER, 2004, 45 (06) :1895-1902

[8] Thin polymer layers formed by polyelectrolyte multilayer techniques on biological surfaces [J].

Elbert, DL ;

Herbert, CB ;

Hubbell, JA .

LANGMUIR, 1999, 15 (16) :5355-5362

[9] Beaded nanofibers formed during electrospinning [J].

Fong, H ;

Chun, I ;

Reneker, DH .

POLYMER, 1999, 40 (16) :4585-4592

[10]

Gittins DI, 2000, ADV MATER, V12, P1947, DOI 10.1002/1521-4095(200012)12:24<1947::AID-ADMA1947>3.3.CO

← 1 2 3 4 →