Synthesis of solid solutions in the (1-x)PbZrO3-xK0.5Bi0.5TiO3 system

被引：5

作者：

Zaremba, T ^{[1
]}

机构：

[1] Silesian Tech Univ, Inst Chem Inorgan Technol & Electrochem, PL-44100 Gliwice, Poland

来源：

JOURNAL OF THERMAL ANALYSIS AND CALORIMETRY | 1998年 / 54卷 / 01期

关键词：

DTA; IR; K0.5Bi0.5TiO3; PbZrO3; solid solution; TG; XRD;

D O I：

10.1023/A:1010104632455

中图分类号：

O414.1 [热力学];

学科分类号：

摘要：

DTA, TG, XRD and IR methods were used to study the formation of solid solutions in the selected subsolidus range of the PbZrO3-K0.5Bi0.5TiO3 system by heating mixtures prepared using oxide substrates, i.e. PbO, Bi2O3, ZrO2, TiO2 and K2CO3. It was found that solid solutions are formed in the reaction of PbO and ZrO2 with intermediate compound, i.e. K0.5Bi0.5TiO3. PbZrO3 was not found to be formed as an intermediate phase.

引用

页码：63 / 69

页数：7

共 10 条

[1] REACTION-MECHANISMS IN THE FORMATION OF PZT SOLID-SOLUTIONS [J].

CHANDRATREYA, SS ;

FULRATH, RM ;

PASK, JA .

JOURNAL OF THE AMERICAN CERAMIC SOCIETY, 1981, 64 (07) :422-425

[2]

EMELYANOV SM, 1983, FIZ TVERD TELA+, V25, P1542

[3]

KINGON AI, 1982, CERAM INT, V8, P108

[4] OBSERVED PHASE-TRANSFORMATIONS OF OXALATE-DERIVED LEAD MONOXIDE POWDER [J].

MUNSON, MJ ;

RIMAN, RE .

JOURNAL OF THERMAL ANALYSIS, 1991, 37 (11-12) :2555-2566

[5]

OKAZAKI K, 1976, CERAMICS ENG DIELECT, P108

[6]

ROGOVA SP, 1986, P 2 C FERR PHYS CHER, V1, P209

[7]

SMOLENSKII GA, 1971, FERROELECTRICS ANTIF, P422

[8]

VENEVTSEV YN, 1985, FERROELECTRIC ANTIFE, P166

[9]

VENKATARAMANI S, 1980, AM CERAM SOC BULL, V59, P462

[10]

ZAREMBA T, 1993, 3 EUROCERAMICS, V2, P133

← 1 →