Structural origin of perpendicular magnetic anisotropy in Ni-W thin films

被引:39
作者
Sulitanu, N [1 ]
机构
[1] Al I Cuza Univ, Dept Solid State Phys, Iasi 6600, Romania
关键词
microstructure; magnetic anisotropy; ferromagnetic films;
D O I
10.1016/S0304-8853(01)00041-5
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
The magnetic properties and microstructure of electrodeposited Ni-W thin films (0-11.7 at% W in composition) were studied. The film structures were divided into three regions: an FCC nanocrystalline phase (0-2 at% W), a transition region from FCC nanocrystalline to amorphous phase (2-7 at% W), and an amorphous phase (> 7 at% W). In the transition region, (4-5at% W) films with perpendicular magnetic anisotropy (PMA) were found. The saturation magnetization, magnetic anisotropy field, perpendicular magnetic anisotropy and perpendicular coercivity for a typical Ni-W film (4.5 at% W) were 420 kA/m, 451 kA/m, 230 kJ/m and 113 kA/m, respectively. The microstructure of Ni-W films with PMA is composed of isolated columnar crystalline grains (27-36 nm) with the FCC phase surrounded by the Ni-W amorphous phase. The appearance of the interface between the magnetic core of Ni crystalline grains and the Ni-W non-magnetic boundary layer seems to be the driving mechanism for the appearance of PMA. The origin of PMA in Ni-W films is mainly attributed to the magnetoelastic anisotropy associated with in-plane internal stress and positive magnetostriction. The secondary source of PMA is believed to be the magnetocrystalline anisotropy of <1 1 1 > columnar grains and its shape magnetic anisotropy. It is concluded that Ni-W electrodeposited films (4-5 at% W) may be applicable for perpendicular magnetic recording media. (C) 2001 Elsevier Science B.V. All rights reserved.
引用
收藏
页码:85 / 93
页数:9
相关论文
共 27 条
[1]   Magnetic anisotropy and its microstructural origin in epitaxially grown SmCo thin films [J].
Benaissa, M ;
Krishnan, KM ;
Fullerton, EE ;
Jiang, JS .
IEEE TRANSACTIONS ON MAGNETICS, 1998, 34 (04) :1204-1206
[2]   PARTICLE INTERACTION PHENOMENA [J].
BERTRAM, HN .
IEEE TRANSACTIONS ON MAGNETICS, 1986, 22 (05) :460-465
[3]   Rotational hysteresis in particles for magnetic recording with different switching modes [J].
Bottoni, G .
JOURNAL OF MAGNETISM AND MAGNETIC MATERIALS, 1996, 155 (1-3) :16-18
[4]   Rotational hysteresis model for stressed ferromagnetic films [J].
Callegaro, L ;
Puppin, E .
IEEE TRANSACTIONS ON MAGNETICS, 1997, 33 (02) :1007-1011
[5]   ABINITIO CALCULATIONS OF THE ELECTRONIC-STRUCTURE OF IMPURITIES AND ALLOYS OF FERROMAGNETIC TRANSITION-METALS [J].
DEDERICHS, PH ;
ZELLER, R ;
AKAI, H ;
EBERT, H .
JOURNAL OF MAGNETISM AND MAGNETIC MATERIALS, 1991, 100 (1-3) :241-260
[7]   Simulation of structural anisotropy in rare-earth transition metal multilayers [J].
Fujiwara, Y ;
Masaki, T ;
Yu, XY ;
Tsunashima, S ;
Iwata, S .
JOURNAL OF MAGNETISM AND MAGNETIC MATERIALS, 1998, 177 :1173-1174
[8]   Influence of the cubic anisotropy constants on the hysteresis loops of single-domain particles:: A Monte Carlo study [J].
García-Otero, J ;
Porto, M ;
Rivas, J ;
Bunde, A .
JOURNAL OF APPLIED PHYSICS, 1999, 85 (04) :2287-2292
[9]   ELECTRODEPOSITION OF THIN MAGNETIC PERMALLOY FILMS [J].
GIRARD, R .
JOURNAL OF APPLIED PHYSICS, 1967, 38 (03) :1423-&
[10]   Thin film magnetic recording media [J].
Grundy, PJ .
JOURNAL OF PHYSICS D-APPLIED PHYSICS, 1998, 31 (21) :2975-2990