Effect of hard polymer filler particles on polymer diffusion in a low-Tg latex film

被引:42
作者
Feng, JR [1 ]
Odrobina, E [1 ]
Winnik, MA [1 ]
机构
[1] Univ Toronto, Dept Chem, Toronto, ON M5S 3H6, Canada
关键词
D O I
10.1021/ma980117w
中图分类号
O63 [高分子化学(高聚物)];
学科分类号
070305 ; 080501 ; 081704 ;
摘要
The intercelluar diffusion of poly(butyl methacrylate) (PBMA; glass transition temperature (T-g) = 21 degrees C) at 60 degrees C was monitored by fluorescence energy transfer in films formed from blends of PBMA latex and a high-T-g (hard) latex. Two types of hard latexes were used in blends: one composed of poly(methyl methacrylate) (PMMA) and the other having a high-T-g shell made of styrene and acrylic monomer units with a large central void (Rohm & Haas Ropaque, ROP). The diffusion rate of PBMA is significantly decreased in the presence of hard particles. The mean apparent diffusion coefficient (D-app) decreased from 0.3 to 0.2 nm(2)/s when 35 vol % ROP particles (400 Mn) are present in the film and to 0.1 nm(2)/s at 75 vol % ROP. The presence of similar-sized PMMA (400 nm) particles showed a slightly larger effect than ROP on the PBMA diffusion: D-app decreased by a factor of 2 at 35 vol % PMMA and a factor of 4 at 75 vol % PMMA. At a constant volume fraction of the hard particle additive, the PBMA diffusion rate decreases significantly when the diameter of PMMA particles is reduced from 400 to 67 nm. These effects can be explained in terms of a model in which a more rigid PBMA layer forms, with a slower diffusion rate, near the hard particle surface.
引用
收藏
页码:5290 / 5299
页数:10
相关论文
共 73 条
[1]   FILLER PARTICLE SIZE AND MECHANICAL PROPERTIES OF POLYMERS [J].
ALTER, H .
JOURNAL OF APPLIED POLYMER SCIENCE, 1965, 9 (04) :1525-&
[2]   ON THE INFLUENCE OF HARD WALLS ON STRUCTURAL-PROPERTIES IN POLYMER GLASS SIMULATION [J].
BASCHNAGEL, J ;
BINDER, K .
MACROMOLECULES, 1995, 28 (20) :6808-6818
[3]   FILM FORMATION WITH LATEX-PARTICLES [J].
CHEVALIER, Y ;
PICHOT, C ;
GRAILLAT, C ;
JOANICOT, M ;
WONG, K ;
MAQUET, J ;
LINDNER, P ;
CABANE, B .
COLLOID AND POLYMER SCIENCE, 1992, 270 (08) :806-821
[4]  
Crank J., 1974, MATH DIFFUSION
[5]   A RECONSIDERATION OF THE MEASUREMENT OF POLYMER INTERDIFFUSION BY FLUORESCENCE NONRADIATIVE ENERGY-TRANSFER [J].
DHINOJWALA, A ;
TORKELSON, JM .
MACROMOLECULES, 1994, 27 (17) :4817-4824
[6]   INTERFACIAL EFFECTS ON THE NMR OF COMPOSITE POLYMERS [J].
DOUGLASS, DC ;
MCBRIERTY, VJ .
POLYMER ENGINEERING AND SCIENCE, 1979, 19 (14) :1054-1063
[7]   HIGH-RESOLUTION SOLID-STATE NMR INVESTIGATION OF THE FILLER-RUBBER INTERACTION .1. HIGH-SPEED H-1 MAGIC-ANGLE-SPINNING NMR-SPECTROSCOPY IN CARBON-BLACK FILLED STYRENE-BUTADIENE RUBBER [J].
DUTTA, NK ;
CHOUDHURY, NR ;
HAIDAR, B ;
VIDAL, A ;
DONNET, JB ;
DELMOTTE, L ;
CHEZEAU, JM .
POLYMER, 1994, 35 (20) :4293-4299
[8]   Mechanistic considerations of particle size effects on film properties of hard/soft latex blends [J].
Eckersley, ST ;
Helmer, BJ .
JOURNAL OF COATINGS TECHNOLOGY, 1997, 69 (864) :97-107
[9]   A NEW MULTIPLET-CLUSTER MODEL FOR THE MORPHOLOGY OF RANDOM IONOMERS [J].
EISENBERG, A ;
HIRD, B ;
MOORE, RB .
MACROMOLECULES, 1990, 23 (18) :4098-4107
[10]  
FARINHA J, 1994, MACROMOLECULES, V27, P4817