Fracture toughness of Zr55Al10Ni5Cu30 bulk metallic glass by 3-point bend testing

被引:58
作者
Kawashima, A [1 ]
Kurishita, H
Kimura, H
Zhang, T
Inoue, A
机构
[1] Tohoku Univ, Inst Mat Res, Int Res Ctr Nucl Mat Sci, Oarai, Ibaraki 3111313, Japan
[2] Tohoku Univ, Inst Mat Res, Sendai, Miyagi 9808577, Japan
[3] BeiHang Univ, Dept Mat Sci & Engn, Beijing 100083, Peoples R China
关键词
Zr55Al10Ni5Cu30 bulk metallic glass; plane strainfracture toughness; three-point bend testing; fatigue precrack; notched specimen; precracked specimen; specimen thickness; vein fracture pattern; microstructure;
D O I
10.2320/matertrans.46.1725
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
In order to evaluate the fracture toughness of a Zr55Al10Ni5CU30 bulk metallic glass and to identify possible sources associated with data variability of Zr-based metallic glasses, three-point bending (3PB) precracked and notched specimens with thicknesses of 2.0 to 2.9 mm were prepared. Miniaturized 34 specimens were subjected to plane strain fracture toughness tests at room temperature. The measured fracture toughness values are in a range of 35.9-76.2 MPam(1/2) and 20 specimens satisfy the K-IC criterion, the K-IC being in a range of 35.9-50.3 MPam(1/2) with an average of 43.3 MPam(1/2). No appreciable difference in fracture toughness is observed between the precracked and notched specimens with root radii of 0.06 and 0.13 mm. Whereas the fracture toughness value varies significantly for each of the precracked and notched specimens. Fracture surfaces show not only a vein pattern typical of fully amorphous alloys but also a flower-like pattern which is less resistant to fracture. All specimens with the entire fracture surface of the vein pattern exhibit very high K-Q values of 70.0-76.2MPam(1/2). The cause of large variability in the fracture toughness data including literature data is discussed.
引用
收藏
页码:1725 / 1732
页数:8
相关论文
共 13 条
[1]   Fracture toughness determination for a beryllium-bearing bulk metallic glass [J].
Conner, RD ;
Rosakis, AJ ;
Johnson, WL ;
Owen, DM .
SCRIPTA MATERIALIA, 1997, 37 (09) :1373-1378
[2]  
FUJITA K, 2005, IN PRESS J METASTABE
[3]   Mechanisms for fracture and fatigue-crack propagation in a bulk metallic glass [J].
Gilbert, CJ ;
Schroeder, V ;
Ritchie, RO .
METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1999, 30 (07) :1739-1753
[4]   Fracture toughness and fatigue-crack propagation in a Zr-Ti-Ni-Cu-Be bulk metallic glass [J].
Gilbert, CJ ;
Ritchie, RO ;
Johnson, WL .
APPLIED PHYSICS LETTERS, 1997, 71 (04) :476-478
[5]   PREPARATION OF BULKY AMORPHOUS ZR-AL-CO-NI-CU ALLOYS BY COPPER MOLD CASTING AND THEIR THERMAL AND MECHANICAL-PROPERTIES [J].
INOUE, A ;
ZHANG, T ;
MASUMOTO, T .
MATERIALS TRANSACTIONS JIM, 1995, 36 (03) :391-398
[6]   MG-CU-Y BULK AMORPHOUS-ALLOYS WITH HIGH-TENSILE STRENGTH PRODUCED BY A HIGH-PRESSURE DIE-CASTING METHOD [J].
INOUE, A ;
NAKAMURA, T ;
NISHIYAMA, N ;
MASUMOTO, T .
MATERIALS TRANSACTIONS JIM, 1992, 33 (10) :937-945
[7]   Fabrication of bulk glassy Zr55Al10Ni5Cu30 alloy of 30 mm in diameter by a suction casting methodQ [J].
Inoue, A ;
Zhang, T .
MATERIALS TRANSACTIONS JIM, 1996, 37 (02) :185-187
[8]   Preparation of bulk glassy Pd40Ni10Cu30P20 alloy of 40 mm in diameter by water quenching [J].
Inoue, A ;
Nishiyama, N ;
Matsuda, T .
MATERIALS TRANSACTIONS JIM, 1996, 37 (02) :181-184
[9]   Application of Zr-based bulk glassy alloys to golf clubs [J].
Kakiuchi, H ;
Inoue, A ;
Onuki, M ;
Takano, Y ;
Yamaguchi, T .
MATERIALS TRANSACTIONS, 2001, 42 (04) :678-681
[10]   Fracture toughness of JLF-1 by miniaturized 3-point bend specimens with 3.3-7.0 mm thickness [J].
Kurishita, H ;
Yamamoto, T ;
Nagasaka, T ;
Nishimura, A ;
Muroga, T ;
Jitsukawa, S .
MATERIALS TRANSACTIONS, 2004, 45 (03) :936-941