Mechanomaking of high speed steel AISI M2: powder consolidation

被引：6

作者：

Matteazzi, P ^{[1
]}

Wolf, F ^{[1
]}

机构：

[1] Univ Udine, Dipartimento Sci & Tecnol Chim, I-33100 Udine, Italy

来源：

MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING | 1998年 / 248卷 / 1-2期

关键词：

nanophase materials; high speed steels; hot isostatic pressing; densification modeling;

D O I：

10.1016/S0921-5093(98)00525-5

中图分类号：

TB3 [工程材料学];

学科分类号：

0805 ; 080502 ;

摘要：

AISI M2 powders were produced from the elements by mechanomaking, a room temperature process driven by high energy ball milling. The as-mechanomade powders with relative densities 0.5, were consolidated by cold and then hot isostatic pressing. Fully dense solids with carbide sizes around 20 nm are obtained after Hot Isostatic Pressing (HIP) at 950 degrees C, while the matrix is constituted of a very fine array of crystallites below 10 nm. An as-quenched hardness of 69 HRC was obtained and a Hall-Petch behavior was observed for Vickers hardness. No evidence of residual austenite was found in either as-HIPed or quenched samples. (C) 1998 Elsevier Science S.A. All rights reserved.

引用

页码：19 / 34

页数：16

共 28 条

[1]

ARTZT E, 1983, METALLURGICAL T A, V14, P211

[2]

ASHBY MF, 1990, HIP MAPS 6 1 SOFTWAR

[3]

*ASM INT, 1990, MET HDB POWD MET, V7, P375

[4] DESIGNING A HIGH-ENERGY BALL-MILL FOR SYNTHESIS OF NANOPHASE MATERIALS IN LARGE QUANTITIES [J].

BASSET, D ;

MATTEAZZI, P ;

MIANI, F .

MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 1993, 168 (02) :149-152

[5]

BEISS P, 1985, MODERN DEV POWDER ME, V17, P331

[6]

BENJAMIN JS, 1970, METALL TRANS, V1, P2943

[7]

BIENVENU Y, 1994, REV METALL CIT, V5, P693

[8]

BLETZ RJ, 1992, ADV POWDER METALL PA, V7, P369

[9] MECHANICAL ACTIVATION OF SOLIDS AND ITS APPLICATION TO TECHNOLOGY [J].

BOLDYREV, VV .

JOURNAL DE CHIMIE PHYSIQUE ET DE PHYSICO-CHIMIE BIOLOGIQUE, 1986, 83 (11-12) :821-829

[10] A SIMPLE, MIXTURES-BASED MODEL FOR THE GRAIN-SIZE DEPENDENCE OF STRENGTH IN NANOPHASE METALS [J].

CARSLEY, JE ;

NING, J ;

MILLIGAN, WW ;

HACKNEY, SA ;

AIFANTIS, EC .

NANOSTRUCTURED MATERIALS, 1995, 5 (04) :441-448

← 1 2 3 →