DGEBA monomer as a solvent for syndiotactic polystyrene

被引:9
作者
Schut, J
Stamm, M
Dumon, M
Gérard, JF
机构
[1] Inst Natl Sci Appl, IMP, LMM, CNRS,UMR 5627, F-69621 Villeurbanne, France
[2] Polymer Res Inst, D-01069 Dresden, Germany
关键词
blends; crystallization; phase diagram; reactive solvent; syndiotactic polystyrene;
D O I
10.1002/masy.200350830
中图分类号
O63 [高分子化学(高聚物)];
学科分类号
070305 ; 080501 ; 081704 ;
摘要
Syndiotactic polystyrene (sPS) has to be processed at high temperatures (i.e. >290degreesC due to its melting point of 270degreesC), which approaches its degradation temperature. We aim to facilitate the processing of sPS by lowering its melt temperature and viscosity with a curable epoxy/amine model system as reactive solvent, which will result in a thermoplastic-thermoset polymer blend. As a first step we therefore investigated the melting behaviour of sPS in epoxy monomer, established its phase diagram, and investigated the crystalline form of sPS in these mixtures. DGEBA epoxy monomer is found to be a solvent for syndiotactic polystyrene at temperatures above 220degreesC. The DGEBA-sPS phase diagram was established by means of DSC, on the basis of crystallization and melting peaks. The form of the curve in the phase diagram indicates that DGEBA is a poor solvent for sPS. In WAXS studies of blends only the P crystalline form was detected, not the 8 form, thus no sPS-DGEBA polymer-solvent compounds (clathrates) were detected. However, DGEBA can still serve as a monomer for improved processing as it depresses the crystallization temperature by 20 to 60 K upon addition of 20 to 90 wt% DGEBA respectively, while a 16 to 45 K melting peak depression can be observed by adding 20 to 90 wt % DGEBA.
引用
收藏
页码:355 / 362
页数:8
相关论文
共 12 条
[1]   The crystallisation of blends of syndiotactic polystyrene and polyphenylene ether [J].
Duff, S ;
Tsuyama, S ;
Iwamoto, T ;
Fujibayashi, F ;
Birkinshaw, C .
POLYMER, 2001, 42 (03) :991-1000
[2]   Guest conformation and diffusion into amorphous and emptied clathrate phases of syndiotactic polystyrene [J].
Guerra, G ;
Manfredi, C ;
Musto, P ;
Tavone, S .
MACROMOLECULES, 1998, 31 (04) :1329-1334
[3]   POLYMORPHISM IN MELT CRYSTALLIZED SYNDIOTACTIC POLYSTYRENE SAMPLES [J].
GUERRA, G ;
VITAGLIANO, VM ;
DEROSA, C ;
PETRACCONE, V ;
CORRADINI, P .
MACROMOLECULES, 1990, 23 (05) :1539-1544
[4]   CRYSTALLINE SYNDIOTACTIC POLYSTYRENE [J].
ISHIHARA, N ;
SEIMIYA, T ;
KURAMOTO, M ;
UOI, M .
MACROMOLECULES, 1986, 19 (09) :2464-2465
[5]   Molecular dimensions in the δ and γ phases of syndiotactic polystyrene, using small angle neutron scattering [J].
Moyses, S ;
Spells, SJ .
POLYMER, 1999, 40 (12) :3269-3274
[6]   An in situ SAXS/WAXS/Raman spectroscopy study on the phase behavior of syndiotactic polystyrene (sPS)/solvent systems: Compound formation and solvent (dis)ordering [J].
Rastogi, S ;
Goossens, JGP ;
Lemstra, PJ .
MACROMOLECULES, 1998, 31 (09) :2983-2998
[7]  
Reverchon E, 1999, J APPL POLYM SCI, V74, P2077, DOI 10.1002/(SICI)1097-4628(19991121)74:8<2077::AID-APP24>3.0.CO
[8]  
2-I
[9]   Relationships between polymorphic crystals and multiple melting peaks in crystalline syndiotactic polystyrene [J].
Sun, YS ;
Woo, EM .
MACROMOLECULES, 1999, 32 (23) :7836-7844
[10]  
Sun YS, 2000, J POLYM SCI POL PHYS, V38, P3210, DOI 10.1002/1099-0488(20001215)38:24<3210::AID-POLB20>3.0.CO