Optimisation of ladle slag composition by application of sulphide capacity model

被引：51

作者：

Andersson, MAT ^{[1
]}

Jönsson, PG

Hallberg, M

机构：

[1] Royal Inst Technol, Dept Met, S-10044 Stockholm, Sweden

[2] Ovako Steel AB, S-81382 Hofors, Sweden

来源：

IRONMAKING & STEELMAKING | 2000年 / 27卷 / 04期

关键词：

D O I：

10.1179/030192300677570

中图分类号：

TF [冶金工业];

学科分类号：

0806 [冶金工程];

摘要：

The sulphur distribution ratio for ladle slags at Ovako Steel AB has been determined by calculating the sulphide capacity using the Royal Institute of Technology (KTH) model and the alumina activity via an empirical expression suggested by Ohta and Suite, and by using the well established theories for sulphur refining. A parameter study was carried out based on plant data from a previous study on desulphurisation, The effect of carbon and aluminium in the steel, the temperature of the steel, and alumina and lime in the slag on the sulphur distribution ratio was investigated, it was shown that the Al2O3/CaO ratio had the largest influence on the conditions studied, and that when it increased the sulphur distribution ratio decreased. Based on these results, new plant trials were carried out, in which the alumina content in the slag was changed. The calculated sulphur distribution ratios for these trials were found to be in good agreement with experimentally determined sulphur distribution ratios. It is concluded that the present approach can be used to optimise multicomponent ladle slags with respect to sulphur refining. I&S/1493.

引用

页码：286 / 293

页数：8

共 17 条

[1]

Application of the sulphide capacity concept on high-basicity ladle slags used in bearing-steel production [J].

Andersson, MAT ;

Jönsson, PG ;

Nzotta, MM .

ISIJ INTERNATIONAL, 1999, 39 (11) :1140-1149

[2]

ENGH TA, 1992, PRINCIPLES METAL REF, P62

[3]

THE BEHAVIOUR OF SULPHUR IN SILICATE AND ALUMINATE MELTS [J].

FINCHAM, CJB ;

RICHARDSON, FD .

PROCEEDINGS OF THE ROYAL SOCIETY OF LONDON SERIES A-MATHEMATICAL AND PHYSICAL SCIENCES, 1954, 223 (1152) :40-62

[4]

GORNERUP M, 1997, 53 TRITA TPM DEP MET

[5]

Hayes P, 1993, PROCESS PRINCIPLES M, P633

[6]

Huet L, 1997, STEEL INT, V21, P47

[7]

JONSSON PG, 1997, P C CLEAN STEEL 5 BA, P218

[8]

LUND TB, 1996, P 5 INT S BEAR STEEL, P124

[9]

NILSSON R, 1995, P SCAN 7 MEF LUL SWE, P149

[10]

Sulphide capacities in some multi component slag systems [J].

Nzotta, MM ;

Sichen, D ;

Seetharaman, S .

ISIJ INTERNATIONAL, 1998, 38 (11) :1170-1179

← 1 2 →