Microstructural evidence for short-circuit oxygen diffusion paths in the oxidation of a dilute Ni-Cr alloy

被引:23
作者
Kim, CK
Hobbs, LW
机构
[1] Massachusetts Institute of Technology, Cambridge, MA 02139
来源
OXIDATION OF METALS | 1996年 / 45卷 / 3-4期
关键词
short-circuit diffusion path; photolithographic marker; Ni and Ni-1 at% Cr oxidation;
D O I
10.1007/BF01046984
中图分类号
TF [冶金工业];
学科分类号
0806 ;
摘要
A comparative study of high-temperature oxidation of Ni containing I at.% Cr and pure Ni was carried out. Instead of the conventional kinetics study using thermogravimetry, a microlithographic marker experiment was designed. Observation of the markers using cross-sectional TEM and SEM has revealed striking differences in the scale morphology, microstructures, and oxidation mechanisms between pure Ni and the Cr-doped Ni substrates. In particular, the results suggest that a small addition of Cr promotes significant inward transport of oxygen. Marker experiments revealed that NiO grown on pure Ni is wholly attributable to outward-cation diffusion. In contrast, NiO grown on Ni-1 at.% Cr exhibited formation of a substantial inner layer having a submicron grain size, established by the markers lo have formed from oxygen ingress. For pure Ni, voids were observed to be distributed only within oxide grains. In contrast, for Ni containing 1 at.% Cr, elongated pores formed extensively along oxide-grain boundaries. Formation of new fine-grain oxide in these pores was observed to have sometimes completely resealed the void. It is, therefore, proposed that the transport of oxygen in the case of oxide scale grown on Ni-1 at.% Cr occurs via voids (pores) formed by vacancy coalescence at the grain boundaries.
引用
收藏
页码:247 / 265
页数:19
相关论文
共 33 条
[1]  
ATKINSON A, 1988, MATER SCI TECH SER, V4, P1046, DOI 10.1179/026708388790221340
[2]   TRANSPORT OF NICKEL AND OXYGEN DURING THE OXIDATION OF NICKEL AND DILUTE NICKEL CHROMIUM-ALLOY [J].
ATKINSON, A ;
SMART, DW .
JOURNAL OF THE ELECTROCHEMICAL SOCIETY, 1988, 135 (11) :2886-2893
[3]  
ATKINSON A, 1987, AERER12762 UKAEA
[4]  
ATKINSON A, 1987, AERER12404 UKAEA
[5]  
ATKINSON A, 1985, AERER11763 UKAEA
[6]  
ATKINSON A, 1987, AERER12751 UKAEA
[7]  
ATKINSON HV, 1988, MATER SCI TECH SER, V4, P1052, DOI 10.1179/026708388790221250
[8]   MICROSTRUCTURE OF ALUMINA SCALES FORMED ON NICOCRAL ALLOYS WITH AND WITHOUT YTTRIUM [J].
CHOQUET, P ;
MEVREL, R .
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 1989, 120 :153-159
[9]  
COTELL CM, 1986, FUNDAMENTAL ASPECTS, V2, P103
[10]  
Evans A. G., 1989, Materials Science Forum, V43, P243, DOI 10.4028/www.scientific.net/MSF.43.243