Joint properties of friction stir welded AZ31B-H24 magnesium alloy

The weldability of friction stir welded hot rolled AZ31B-H24 magnesium alloy sheet, 4 mm in thickness, was evaluated, varying welding parameters such as tool rotation speed and travel welding speed. Sound welding conditions depended mainly on sufficient heat input during the welding process. Insufficient heat input, which was generated in the case of higher travel speed and lower rotation speed, caused an inner void or lack of bonding in the stir zone. The microstructure of the weld zone was composed of five regions: base metal, heat affected zone, thermomechanically affected zone, stir zone I and stir zone II. Unlike the general feature of friction stir welded aluminium alloys, the grain size of the weld zone was larger than that of the base metal. Stir zones I and 11 were characterised by partial dynamic recrystallisation and full dynamic recrystallisation, respectively. The hardness of the weld zone was lower than that of the base metal owing to grain growth. A wider range of defect free welding conditions was acquired at higher tool rotation speed and lower welding speed. The maximum tensile strengh was 240 MPa, which was similar to85% of the base metal value of 293 MPa. The fracture location was close to the stir zone.