Thermotropic liquid-crystalline polyesters of 4,4′-biphenol and phenyl-substituted 4,4′-biphenols with 4,4′-oxybisbenzoic acid

A series of thermotropic polyesters, derived from 4,4'-biphenol (BP), 3-phenyl-4,4'-biphenol (MPBP), and 3,3'-bis(phenyl)-4,4'-biphenol (DPBP), 4,4'-oxybisbenzoic acid (4,4'-OBBA), and other aromatic dicarboxylic acids as comonomers, were prepared by melt polycondensation and were characterized for their thermotropic liquid-crystalline (LC) properties with a variety of experimental techniques. The homopolymer of BP with 4,4'-OBBA and its copolymers with either 50 mol % terephthalic acid or 2,6-naphthalenedicarboxylic acid had relatively high values of the crystal-to-nematic transition (448-460 degreesC), above which each of them formed. a nematic LC phase. In contrast, the homopolymers of MPBP and DPBP had low fusion temperatures and low isotropization temperatures and formed nematic melts above the fusion temperatures. Each of these two polymers also exhibited two glass-transition temperatures, which were associated with vitrified noncrystalline (amorphous) regions and vitrified LC domains, as obtained directly from melt polycondensation. As expected, they had higher glass-transition temperatures (176-211 degreesC) than other LC polyesters and had excellent thermal stability (516-567 degreesC). The fluorescence properties of the homopolymer of DPBP with 4,4'-OBBA, which was soluble in common organic solvents such as chloroform and tetrahydrofuran, were also included in this study. For example, it had an absorption spectrum (lambda (max) = 259 and 292 nm), an excitation spectrum (lambda (ex) = 258 and 292 nm with monitoring at 350 nm), and an emission spectrum (lambda (em) = 378 nm with excitation at 330 nm) in chloroform. (C) 2001 John Wiley & Sons, Inc.