Bulk moduli and high-pressure crystal structures of minium, Pb3O4, determined by X-ray powder diffraction

We report the pressure dependence of the crystal structure of lead tetroxide (P less than or equal to 41.05 GPa, T 298 K) using high-resolution angle-dispersive X-ray powder diffraction. Pb3O4 shows two reversible phase transitions in the measured pressure range. The crystal structures of the modifications identified have in common frameworks of Pb+4O6 octahedra and irregular Pb+2O4+1 respectively Pb2+O6+1 polyhedra. At ambient conditions, Pb3O4 crystallizes in space group P4(2)/mbc (phase 1). Between 0.11 and 0.3 GPa it exhibits a displacive second order phase transition to a structure with space group Pbam (phase II). A second displacive phase transition occurs between 5.54 and 6.6 GPa to another structure with space group Pbam (phase 111) but halved c dimension. A non-linear compression behavior over the entire pressure range is observed, which can be described by two Vinet relations in the ranges from 0.28 to 5.54 GPa and from 6.6 to 41.05 GPa. The extrapolated bulk moduli of the high-pressure phases were determined to be K-0 = 21(2) GPa for phase 11 and K-0 = 91(3) GPa for phase III. The crystal structures of all phases were refined from X-ray diffraction powder data collected at several pressures between 0.06 and 41.05 GPa. Except for their cell dimensions, phases I and 11 were found to be isostructural to the corresponding phases at low temperatures, whereas phase III can be derived from the Sr2PbO4 aristotype. With increasing pressure, the lone pair which is localized at Pb2+ adopts increasingly pure s-character, which is reflected by the similar coordination polyhedra of Ph2+ in Pb3O4 (phase 111) and of Sr2+ in Sr2PbO4.