Preparation and electrical properties of a pyrochlore-related Ce2Zr2O8-x phase

被引：21

作者：

Hui, Z ^{[1
]}

Nicolas, G ^{[1
]}

Françoise, V ^{[1
]}

Michèle, P ^{[1
]}

机构：

[1] Ecole Natl Super Mines, LPMG, CNRS 2021, Ctr SPIN, F-42023 St Etienne 2, France

来源：

SOLID STATE IONICS | 2003年 / 160卷 / 3-4期

关键词：

Ce0.5Zr0.5O2; reduction-oxidation; pyrochlore phase; conductivity; cathode;

D O I：

10.1016/S0167-2738(03)00207-8

中图分类号：

O64 [物理化学（理论化学）、化学物理学];

学科分类号：

070304 ; 081704 ;

摘要：

A pyrochlore-related Ce2Zr2O8-x phase has been prepared in a reduction reoxidation process from Ce0.5Zr0.5O2 powders. Ce2Zr2O8-x, based on a cubic symmetry with a = 1.053 nm, decomposes in nitrogen at 800 degreesC, but remains stable up to 900 degreesC in air. It shows mixed oxygen ionic and electronic conductivity. The bulk conductivity at 700 degreesC is 4 x 10(-4) S cm(-1) in air and 1 X 10(-2) S cm(-1) in nitrogen, and the activation energy is 1.27 eV in air. In nitrogen, the Arrhenius law is not obeyed, and a curved plot was obtained from 400 to 700 degreesC; then, the conductivity decreased rapidly due to the thermal decomposition of Ce2Zr2O8-x. (C) 2003 Elsevier B.V. All rights reserved.

引用

页码：317 / 326

页数：10

共 29 条

[1] ELECTRICAL-PROPERTIES IN THE ZRO2-CEO2-Y2O3 SYSTEM [J].

ARASHI, H ;

NAITO, H ;

NAKATA, M .

SOLID STATE IONICS, 1995, 76 (3-4) :315-319

[2] Electrical and oxygen storage/release properties of nanocrystalline ceria-zirconia solid solutions [J].

Boaro, M ;

Trovarelli, A ;

Hwang, JH ;

Mason, TO .

SOLID STATE IONICS, 2002, 147 (1-2) :85-95

[3] INDEXING OF POWDER DIFFRACTION PATTERNS FOR LOW-SYMMETRY LATTICES BY THE SUCCESSIVE DICHOTOMY METHOD [J].

BOULTIF, A ;

LOUER, D .

JOURNAL OF APPLIED CRYSTALLOGRAPHY, 1991, 24 (pt 6) :987-993

[4] Electrical properties of the ZrO2-CeO2 system [J].

Chiodelli, G ;

Flor, G ;

Scagliotti, M .

SOLID STATE IONICS, 1996, 91 (1-2) :109-121

[5] Surface and structural characterization of CexZr1-xO2 CEZIRENCAT mixed oxides as potential three-way catalyst promoters [J].

Colón, G ;

Pijolat, M ;

Valdivieso, F ;

Vidal, H ;

Kaspar, J ;

Finocchio, E ;

Daturi, M ;

Binet, C ;

Lavalley, JC ;

Baker, RT ;

Bernal, S .

JOURNAL OF THE CHEMICAL SOCIETY-FARADAY TRANSACTIONS, 1998, 94 (24) :3717-3726

[6] OXYGEN REDUCTION AT LA0.5SR0.5MNO3 THIN-FILM YTTRIA-STABILIZED ZIRCONIA INTERFACE STUDIED BY IMPEDANCE SPECTROSCOPY [J].

GHARBAGE, B ;

PAGNIER, T ;

HAMMOU, A .

JOURNAL OF THE ELECTROCHEMICAL SOCIETY, 1994, 141 (08) :2118-2121

[7] ELECTRICAL CONDUCTIVITY OF SILVER SULFIDE [J].

HEBB, MH .

JOURNAL OF CHEMICAL PHYSICS, 1952, 20 (01) :185-190

[8] Thermal stability of oxygen storage properties in a mixed CeO2-ZrO2 system [J].

Hori, CE ;

Permana, H ;

Ng, KYS ;

Brenner, A ;

More, K ;

Rahmoeller, KM ;

Belton, D .

APPLIED CATALYSIS B-ENVIRONMENTAL, 1998, 16 (02) :105-117

[9] Interfacial polarization characteristics of Pt vertical bar BaCe0.8Gd0.2O3 vertical bar Pt cells at intermediate temperatures [J].

Hu, HX ;

Liu, ML .

JOURNAL OF THE ELECTROCHEMICAL SOCIETY, 1997, 144 (10) :3561-3567

[10] Electrical conductivity of novel tetragonal t′meta-(Ce0.5Zr0.5)O2 phase prepared by reduction and successive oxidation of t′ phase [J].

Izu, N ;

Kishimoto, H ;

Omata, T ;

Otsuka-Yao-Matsuo, S .

JOURNAL OF SOLID STATE CHEMISTRY, 2000, 151 (02) :253-259

← 1 2 3 →