Dissolution of cellulose in aqueous NaOH solutions

Dissolution of a number of cellulose samples in aqueous NaOH was investigated with respect to the influence of molecular weight, crystalline form and the degree of crystallinity of the source samples. A procedure for dissolving microcrystalline cellulose was developed and optimized, and then applied to other cellulose samples of different crystalline forms, crystallinity indices and molecular weights. The optimum conditions involved swelling cellulose in 8-9 wt% NaOH and then freezing it into a solid mass by holding it at -20 degrees C. This was followed by thawing the frozen mass at room temperature and diluting with water to 5% NaOH. All samples prepared from microcrystalline cellulose were completely dissolved in the NaOH solution by this procedure, All regenerated celluloses having either cellulose II or an amorphous structure prepared from linter cellulose and kraft pulps were also essentially dissolved in the aqueous NaOH by this process. The original linter cellulose, its mercerized form and cellulose III samples prepared from it had limited solubility values of only 26-37%, when the same procedure was applied. The differences in the solubility of the celluloses investigated have been interpreted in terms of the degrees to which some long-range orders present in solid cellulose samples have been disrupted in the course of pre-treatments.