Preparation and thermal stability of doped TiO2 composite membranes by the sol-gel process

被引:20
作者
Bae, DS [1 ]
Han, KS
Choi, SH
机构
[1] Korea Inst Sci & Technol, Div Ceram, Seoul 136791, South Korea
[2] Hanyang Univ, Dept Inorgan Mat Engn, Seoul 133791, South Korea
关键词
doped TiO2 composite membrane; sol-gel process; Fe2O3; CeO2; Pt; thermal stability;
D O I
10.1016/S0167-2738(98)00100-3
中图分类号
O64 [物理化学(理论化学)、化学物理学];
学科分类号
070304 ; 081704 ;
摘要
Supported TiO2, composite membranes doped with various elements (Fe2O3, CeO2, Pt) were synthesized by the sol-gel process. The average particle size of the doped TiO2 sol was below 15 nm and well dispersed in the solution. XPS results show the additive to be continuously and homogeneously dispersed in the TiO, membrane. It was observed that the TiO, composite membranes doped with Fe2O3, CeO2, and Pt had higher heat resistance than that of the pure TiO2 composite membrane. The effect of sintering on the change of the mean particle diameter of the several membranes was decreased in the following order: Fe2O3 > CeO2 greater than or equal to Pt. It was observed that the doped TiO2 composite membranes showed a crack-free and homogeneous microstructure as well as a narrow particle size distribution up to above 650 degrees C. (C) 1998 Elsevier Science B.V. All rights reserved.
引用
收藏
页码:239 / 245
页数:7
相关论文
共 15 条
  • [1] BHAVE RR, 1991, INORGANIC MEMBRANES, P15
  • [2] BRINKER CJ, 1990, SOL GEL SCI PHYSICS, P841
  • [3] CERYAN M, 1986, ULTRAFILTRATION HDB, P7
  • [4] PREPARATION AND CHARACTERIZATION OF SOL-GEL DERIVED MICROPOROUS MEMBRANES WITH HIGH THERMAL-STABILITY
    CHAI, MR
    MACHIDA, M
    EGUCHI, K
    ARAI, H
    [J]. JOURNAL OF MEMBRANE SCIENCE, 1994, 96 (03) : 205 - 212
  • [5] A COMPARATIVE-STUDY ON THERMAL AND HYDROTHERMAL STABILITY OF ALUMINA, TITANIA AND ZIRCONIA MEMBRANES
    CHANG, CH
    GOPALAN, R
    LIN, YS
    [J]. JOURNAL OF MEMBRANE SCIENCE, 1994, 91 (1-2) : 27 - 45
  • [6] Derjaguin BV., 1941, ACTA PHYSICOCHIM URS, V14, P633, DOI DOI 10.1016/0079-6816(93)90013-L
  • [7] STUDIES ON THE MIXED-OXIDE CATALYST AL2O3-CR2O3 .1. SURFACE-PROPERTIES
    EZZO, EM
    ELNABARAWY, T
    YOUSSEF, AM
    [J]. SURFACE TECHNOLOGY, 1979, 9 (02): : 111 - 118
  • [8] KUMAR KNP, 1992, MATER RES SOC SYMP P, V271, P499, DOI 10.1557/PROC-271-499
  • [9] NEW INORGANIC ULTRAFILTRATION MEMBRANES - TITANIA AND ZIRCONIA MEMBRANES
    LARBOT, A
    FABRE, JP
    GUIZARD, C
    COT, L
    GILLOT, J
    [J]. JOURNAL OF THE AMERICAN CERAMIC SOCIETY, 1989, 72 (02) : 257 - 261
  • [10] THE PREPARATION AND CHARACTERIZATION OF ALUMINA MEMBRANES WITH ULTRA-FINE PORES
    LEENAARS, AFM
    KEIZER, K
    BURGGRAAF, AJ
    [J]. JOURNAL OF MATERIALS SCIENCE, 1984, 19 (04) : 1077 - 1088