Assessment of TBC systems failure mechanisms using a fracture mechanics approach

被引：197

作者：

Aktaa, J ^{[1
]}

Sfar, K ^{[1
]}

Munz, D ^{[1
]}

机构：

[1] Forschungszentrum Karlsruhe, GmbH Inst Mat Forsch 2, D-76021 Karlsruhe, Germany

来源：

ACTA MATERIALIA | 2005年 / 53卷 / 16期

关键词：

thermal barrier coating (TBC); failure mechanism; finite element method; modified crack closure integral; crack assessment;

D O I：

10.1016/j.actamat.2005.06.003

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

Failure of thermal barrier coating (TBC) systems under thermomechanical loading is very complicated, as it is influenced by many factors, such as thermal mismatch, oxidation, interface roughness, creep, sintering, which have to be more or less taken into account. Determination of the residual stress fields induced yields information about the critical areas for crack nucleation in a first step and may help interpret the experimental observations of the cracking behavior. The calculated residual stresses relevant to failure are highly localized and may be sufficient for crack nucleation, but not for crack propagation and failure. Therefore, a fracture mechanics approach was developed, by means of which cracks are modeled in the critical areas of the TBC system and assessed using the modified crack closure integral method for determining the mode-dependent crack loading. The crack propagation capability is then predicted using a mixed mode failure criterion implemented recently and proper fracture toughness data. Applying this approach, different failure mechanisms observed experimentally for TBC systems are investigated. (c) 2005 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.

引用

页码：4399 / 4413

页数：15

共 25 条

[11]

*HIBB KARLSS SOR, 2000, AB US MAN

[12]

Irwin G.R., 1958, Elasticity and Plasticity/Elastizitat und Plastizitat, P551

[13] The displacement of the thermally grown oxide in thermal barrier systems upon temperature cycling [J].

Karlsson, AM ;

Hutchinson, JW ;

Evans, AG .

MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2003, 351 (1-2) :244-257

[14] Stress development in alumina scales formed upon oxidation of (111)NiAl single crystals [J].

Lipkin, DM ;

Clarke, DR ;

Hollatz, M ;

Bobeth, M ;

Pompe, W .

CORROSION SCIENCE, 1997, 39 (02) :231-242

[15]

MANNSMANN W, 1995, THESIS U KARLSRUHE T

[16] FAILURE MECHANISMS OF THERMAL BARRIER COATINGS EXPOSED TO ELEVATED-TEMPERATURES [J].

MILLER, RA ;

LOWELL, CE .

THIN SOLID FILMS, 1982, 95 (03) :265-273

[17] Characterization of a cyclic displacement instability for a thermally grown oxide in a thermal barrier system [J].

Mumm, DR ;

Evans, AG ;

Spitsberg, IT .

ACTA MATERIALIA, 2001, 49 (12) :2329-2340

[18]

Quadakkers WJ, 1999, ELEVATED TEMPERATURE COATINGS: SCIENCE AND TECHNOLOGY III, P119

[19]

RENUSCH D, 2002, ADV THERMAL BARRIER, P48

[20]

Richard H.A., 1985, BRUCHVORHERSAGEN BEI, V631, P1

← 1 2 3 →