Influence of second phase particles on recrystallisation of cold-rolled low carbon microalloyed steels during isothermal annealing

被引：9

作者：

Capdevila, C ^{[1
]}

De Cock, T ^{[1
]}

García-Mateo, C ^{[1
]}

Caballero, FG ^{[1
]}

de Andrés, CG ^{[1
]}

机构：

[1] CSIC, CENIM, Ctr Nacl Invest Met, Dept Met Phys, E-28040 Madrid, Spain

来源：

MICROALLOYING FOR NEW STEEL PROCESSES AND APPLICATIONS | 2005年 / 500-501卷

关键词：

low carbon steel; recrystallisation; cementite; thermoelectric power;

D O I：

10.4028/www.scientific.net/MSF.500-501.803

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

The recrystallisation behaviour of two cold-rolled low carbon microalloyed steels with different Ti content was investigated by thermoelectric power (TEP) measurements and metallography. It was shown that recrystallisation was more sluggish in the higher Ti grade steel as compare with traditional ELC and LC steels. The existence of Ti in solid solution together with the pinning effect of Nb-, V- and Ti-rich particles are likely to be responsible for such behaviour. Metallographic etching with picral revealed that cementite act as preferential nucleation site for recrystallisation.

引用

页码：803 / 810

页数：8

共 6 条

[1] Characterization by thermoelectric power of a commercial aluminum-iron-silicon alloy (8011) during isothermal precipitation [J].

Luiggi, NJ .

METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1998, 29 (11) :2669-2677

[2]

*NAT PHYS LAB, 1996, MET THERM DAT, P1

[3]

Oatley C. W., 1972, SCANNING ELECT MIC 1

[4]

Ray RK, 1994, INT MATER REV, V39, P129, DOI 10.1179/095066094790326112

[5]

SARDOY V, 1998, P INT S MOD LC ULC S, V1

[6]

URABE T, 1994, ISIJ INT, V34, P441

← 1 →