Creep strengths of Ir-containing 5th generation SC superalloys

被引：5

作者：

Kobayashi, T ^{[1
]}

Harada, H

Osawa, M

Sato, A

机构：

[1] Natl Inst Mat Sci, Mat Engn Lab, High Temp Mat Grp, Tsukuba, Ibaraki 3050047, Japan

[2] Shibaura Inst Technol, Grad Sch, Tokyo 1080023, Japan

来源：

JOURNAL OF THE JAPAN INSTITUTE OF METALS | 2005年 / 69卷 / 12期

关键词：

nickel-base superalloy; single crystal; creep; ruthenium; iridium;

D O I：

10.2320/jinstmet.69.1099

中图分类号：

TF [冶金工业];

学科分类号：

0806 ;

摘要：

Our Ni-base single crystal (SC) superalloys that have been designated as 4(th) and 5(th) generation SC alloys contain Ru for the enhancement of microstructure stability. The authors have previously reported that Ir addition was as effective as Ru for enhancing the microstructure stability. In this paper, Ir was added to TMS-173, a new 5th generation SC alloy, by substituting out Ru. The creep strength of this new SC alloy, designated as TMS-173 (Ir), was then compared to that of the original Ru-containing alloys, TMS-173. Creep tests were conducted for these SC superalloys under several conditions: 800 degrees C/735 MPa, 900 degrees C/392 MPa, 1000 degrees C/245 MPa and 1100 degrees C/137 MPa. The Ir-containing alloys showed shorter creep rupture life than The Ru-containing one in higher temperature and lower stress conditions such as 1100 degrees C/137 MPa. However, at lower temperature and higher stress conditions, The Ir-containing alloy showed longer creep rupture life than Ru-containing one; the former showed 3.2 times longer creep rupture life than the latter in the creep tests at 900 degrees C/392 MPa. Microstructure observations of creep-ruptured specimens confirmed that Ir was as effective as Ru for microstructure stability.

引用

页码：1099 / 1103

页数：5

共 10 条

[1]

Erickson GL, 1996, SUPERALLOYS 1996, P35

[2]

FUJIMURA T, 2004, J GAS TURBINE SOC JA, V32, P174

[3]

HARADA H, 2003, J TURBINE SOC JAPAN, V31, P53

[4]

HARADA H, 1999, SPRINGER SERIES MAT, V34, P39

[5] Influence of heat treatment on microstructure and mechanical properties of 4th generation DS superalloys [J].

Kobayashi, T ;

Koizumi, Y ;

Yokokawa, T ;

Osawa, M ;

Harada, H .

JOURNAL OF THE JAPAN INSTITUTE OF METALS, 2004, 68 (02) :94-97

[6]

Kobayashi T., 1997, P 4 INT C PARS TURB, P766

[7]

Koizumi Y, 2004, Superalloys 2004, P35, DOI 10.7449/2004/Superalloys_2004_35_43

[8] Development of next generation Ni-base single crystal superalloys containing ruthenium [J].

Koizumi, Y ;

Zhang, JX ;

Kobayashi, T ;

Yokokawa, T ;

Harada, H ;

Aoki, Y ;

Arai, M .

JOURNAL OF THE JAPAN INSTITUTE OF METALS, 2003, 67 (09) :468-471

[9] Slip geometry of dislocations related to cutting of the γ′ phase in a new generation single-crystal superalloy [J].

Zhang, JX ;

Murakumo, T ;

Koizumi, Y ;

Kobayashi, T ;

Harada, H .

ACTA MATERIALIA, 2003, 51 (17) :5073-5081

[10] Interfacial dislocation networks strengthening a fourth-generation single-crystal TMS-138 superalloy [J].

Zhang, JX ;

Murakumo, T ;

Koizumi, Y ;

Kobayashi, T ;

Harada, H ;

Masaki, S .

METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 2002, 33 (12) :3741-3746

← 1 →