PTC effect of polyethylene/foliated graphite nanocomposites

被引:9
作者
Chen, GH [1 ]
Lu, JR [1 ]
Wu, DJ [1 ]
机构
[1] Huaqiao Univ, Dept Mat Sci & Engn, Fujian 362021, Peoples R China
基金
中国国家自然科学基金;
关键词
D O I
10.1007/s10853-005-1119-4
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
The PTC effect of polyethylene and foliated graphite (FG) nanocomposites are discussed. The foliated graphite (FG) is prepared by exfoliation of expanded graphite which possess high aspect ratio with diameter ranging from 5 to 20 μm and average thickness of 40nm. For conventional conductive filler such as metallic powders and conventional graphite, low conductive filler concentration composite show a high room resistivity and a low PTC intensity. As a result after the PTC transition, resistivity decreases with increasing temperature, which is defined as the negative temperature coefficient (NTC) effect.
引用
收藏
页码:5041 / 5043
页数:3
相关论文
共 21 条
[1]   TiCl3-doped Ba0.92Ca0.08TiO3 positive temperature coefficient resistance ceramics with low room temperature resistivity [J].
Cao, MH ;
Zhou, DX ;
Gong, SP ;
Hu, YX ;
Cao, ML .
MATERIALS SCIENCE AND ENGINEERING B-SOLID STATE MATERIALS FOR ADVANCED TECHNOLOGY, 2002, 88 (01) :35-39
[2]   TEMPERATURE AND PRESSURE-DEPENDENCE OF THE CONDUCTIVITY ANISOTROPY OF UNIDIRECTIONAL SHORT CARBON-FIBER FILLED POLYMERS [J].
CARMONA, F ;
ELAMARTI, A .
JOURNAL OF MATERIALS RESEARCH, 1992, 7 (01) :117-123
[3]  
CARMONA F, 1980, J PHYS LETT, V41, P531
[4]   Preparation of polystyrene/graphite nanosheet composite [J].
Chen, GH ;
Wu, CL ;
Weng, WG ;
Wu, DJ ;
Yan, WL .
POLYMER, 2003, 44 (06) :1781-1784
[5]   Exfoliation of graphite flake and its nanocomposites [J].
Chen, GH ;
Wu, DJ ;
Weng, WU ;
Wu, CL .
CARBON, 2003, 41 (03) :619-621
[6]   Preparation and characterization of graphite nanosheets from ultrasonic powdering technique [J].
Chen, GH ;
Weng, WG ;
Wu, DJ ;
Wu, CL ;
Lu, JR ;
Wang, PP ;
Chen, XF .
CARBON, 2004, 42 (04) :753-759
[7]   Double positive temperature coefficient effects of carbon black-filled polymer blends containing two semicrystalline polymers [J].
Feng, JY ;
Chan, CM .
POLYMER, 2000, 41 (12) :4559-4565
[8]   Positive temperature coefficient effect in carbon black/epoxy polymer composites [J].
Fournier, J ;
Boiteux, G ;
Seytre, G ;
Marichy, G .
JOURNAL OF MATERIALS SCIENCE LETTERS, 1997, 16 (20) :1677-1679
[9]   The influence of crystalline and aggregate structure on PTC characteristic of conductive polyethylene carbon black composite [J].
Luo, YL ;
Wang, GC ;
Zhang, BY ;
Zhang, ZP .
EUROPEAN POLYMER JOURNAL, 1998, 34 (08) :1221-1227
[10]   ELECTRICAL-CONDUCTION IN CARBON-BLACK COMPOSITES [J].
MEDALIA, AI .
RUBBER CHEMISTRY AND TECHNOLOGY, 1986, 59 (03) :432-454