Method to account for true contact area in soda-lime glass during nanoindentation with the Berkovich tip

An. empirical relationship for estimating the pile-up contact area from the contact stiffness, S and the contact depth, h(c) has been developed. This was achieved first by using the atomic force microscope to image nanoindents made with the Berkovich indenter in soda-lime glass and approximating the pile-up contact perimeter as a semi-ellipse. Then, by determining the pile-up contact area for several peak indentation loads, a correlation was found between the pile-up contact area and the load used to generate it. The importance of this new method of determining the pile-up contact area is that the need for indent imaging is made completely redundant, since the contact stiffness is a quantity that is routinely obtained during nanoindentation data analysis. Elastic modulus of soda-lime glass of 70 +/- 1.5 GPa is measured with loads ranging from 20 to 500 mN. The hardness measured also falls within the range of values, 5.2-5.9 GPa, normally quoted in the literature for the glass. (c) 2005 Elsevier B.V. All rights reserved.