Stretching and Breaking of Ultrathin MoS2

We report on measurements of the stiffness and breaking strength of monolayer MoS2, a new semiconducting analogue of graphene. Single and bilayer MoS2 is exfoliated from bulk and transferred to a substrate containing an array of microfabricated circular holes. The resulting suspended, free-standing membranes are deformed and eventually broken using an atomic force microscope. We find that the In-plane stiffness of monolayer MoS2 is 180 +/- 60 Nm(-1), corresponding to an effective Young's modulus of 270 +/- 100 GPa, which Is comparable to that of steel. Breaking occurs at an effective strain between 6 and 11% with the average breaking strength of 15 +/- 3 Nm(-1) (23 GPa). The strength of strongest monolayer membranes Is 11% of its Young's modulus, corresponding to the upper theoretical limit which indicates that the material can be highly crystalline and almost defect-free. Our results show that monolayer MoS2 could be suitable for a variety of applications such as reinforcing elements in composites and for fabrication of flexible electronic devices.