High coercivity and exchange coupling of Ni/NiO nanocomposite film

被引：29

作者：

Yi, JB ^{[1
]}

Ding, J ^{[1
]}

Zhao, ZL ^{[1
]}

Liu, BH ^{[1
]}

机构：

[1] Natl Univ Singapore, Dept Mat Sci, Singapore 119260, Singapore

来源：

JOURNAL OF APPLIED PHYSICS | 2005年 / 97卷 / 10期

关键词：

D O I：

10.1063/1.1851424

中图分类号：

O59 [应用物理学];

学科分类号：

摘要：

A coercivity of 2.4 kOe was achieved at room temperature after magnetic annealing a pure Ni film at 650 K for 20 min under O-2 partial pressure of 0.001 torr. The interface structure of Ni/NiO during the formation of NiO under magnetic field and the small grains may be responsible for the large coercivity. Additionally, the surface NiO, dipolar interaction of Ni particles, and the composition of NiO inside the film may affect the coercivity as well. C 2005 American Institute of Physics.

引用

页数：3

共 19 条

[1] THEORY OF THE OXIDATION OF METALS [J].

CABRERA, N ;

MOTT, NF .

REPORTS ON PROGRESS IN PHYSICS, 1948, 12 :163-184

[2] EXCHANGE-ANISOTROPY IN COUPLED FILMS OF NI81FE19 WITH NIO AND COXNI1-XO [J].

CAREY, MJ ;

BERKOWITZ, AE .

APPLIED PHYSICS LETTERS, 1992, 60 (24) :3060-3062

[3] Nanostructuue, interfaces, and magnetic properties in giant magnetoresistive NiO-Co-Cu-based spin valves [J].

Chopra, HD ;

Hockey, BJ ;

Chen, PJ ;

McMichael, RD ;

Egelhoff, WF .

JOURNAL OF APPLIED PHYSICS, 1997, 81 (08) :4017-4019

[4] Size dependence of the exchange bias field in NiO/Ni nanostructures [J].

Fraune, M ;

Rüdiger, U ;

Güntherodt, G ;

Cardoso, S ;

Freitas, P .

APPLIED PHYSICS LETTERS, 2000, 77 (23) :3815-3817

[5] THERMAL FLUCTUATION AFTEREFFECT MODEL FOR SOME SYSTEMS WITH FERROMAGNETIC-ANTIFERROMAGNETIC COUPLING [J].

FULCOMER, E ;

CHARAP, SH .

JOURNAL OF APPLIED PHYSICS, 1972, 43 (10) :4190-&

[6] MAGNETIC-PROPERTIES OF ULTRAFINE CO PARTICLES [J].

GANGOPADHYAY, S ;

HADJIPANAYIS, GC ;

SORENSEN, CM ;

KLABUNDE, KJ .

IEEE TRANSACTIONS ON MAGNETICS, 1992, 28 (05) :3174-3176

[7] KINETICS OF REACTION OF OXYGEN WITH CLEAN NICKEL SINGLE-CRYSTAL SURFACES .1. NI(100) SURFACE [J].

HOLLOWAY, PH ;

HUDSON, JB .

SURFACE SCIENCE, 1974, 43 (01) :123-140

[8] Exchange coupling of NiO CoFeB films [J].

Jimbo, M ;

Kurita, J ;

Sakakibara, K ;

Goto, T ;

Shigeoka, T .

JOURNAL OF MAGNETISM AND MAGNETIC MATERIALS, 1999, 198-99 :431-433

[9] THE GROWTH OF IRON-OXIDE, NICKEL-OXIDE AND COBALT OXIDE THIN-FILMS BY LASER-ABLATION FROM METAL TARGETS [J].

KENNEDY, RJ .

IEEE TRANSACTIONS ON MAGNETICS, 1995, 31 (06) :3829-3831

[10] Effects of crystal texture on exchange anisotropy in NiO spin valves [J].

Lee, SS ;

Hwang, DG ;

Park, CM ;

Lee, KA ;

Rhee, JR .

JOURNAL OF APPLIED PHYSICS, 1997, 81 (08) :5298-5300

← 1 2 →