In situ formation of blends by photopolymerization of poly(ethylene glycol) dimethacrylate and polylactide

被引:18
作者
Zhang, K [1 ]
Simon, CG [1 ]
Washburn, NR [1 ]
Antonucci, JM [1 ]
Lin-Gibson, S [1 ]
机构
[1] Natl Inst Stand & Technol, Div Polymers, Gaithersburg, MD 20899 USA
关键词
D O I
10.1021/bm0500648
中图分类号
Q5 [生物化学]; Q7 [分子生物学];
学科分类号
071010 ; 081704 ;
摘要
Blends of cross-linked poly(ethylene glycol) dimethacrylate (PEGDMA) and poly(D,L-lactide) (PLA) were prepared by mixing photoactive PEGDMA (molecular mass: 875 g/mol) and PLA, and subsequently photopolymerizing, the mixture with visible light. The effects of PLA molecular mass and mass fraction on the theological properties of the PEGDMA/PLA mixtures, and on the degree of methacrylate vinyl conversion (DC), as well as blend miscibility, microstructure, mechanical properties, in vitro swelling behavior, and cell responses were studied. PLA-2K (molecular mass: 2096 g/mol) and PLA-63K (molecular mass: 63 000 g/mol) formed miscible and partially miscible blends with cross-linked PEGDMA, respectively. The addition of the PLA-2K did not affect the immediate or post-cure (>24 h) DC of the PEGDMA upon photopolymerization. However, the addition of PLA-63K decreased the immediate DC of the PEGDMA, which can be increased through extending the curing time or post-curing period. Compared to the crosslinked neat PEGDMA and PLA-2K/PEGDMA blends, PLA-63K/PEGDMA blends were significantly stronger, stiffer, and tougher. Both types of blends and the cross-linked PEGDMA swelled when soaked in a phosphate buffered saline (PBS) solution. The attachment and spreading of MCT3-E1 cells increased with increasing PLA-63K content, in the blends. The facile and rapid formation of PEGDMA/PLA blends by photopolymerization represents a simple and efficient approach to a class of biomaterials with a broad spectrum of properties.
引用
收藏
页码:1615 / 1622
页数:8
相关论文
共 35 条
[1]   Structure and mechanical properties of poly(D,L-lactic acid)/poly(ε-caprolactone) blends [J].
Broz, ME ;
VanderHart, DL ;
Washburn, NR .
BIOMATERIALS, 2003, 24 (23) :4181-4190
[2]   Controlling the spatial distribution of ECM components in degradable PEG hydrogels for tissue engineering cartilage [J].
Bryant, SJ ;
Anseth, KS .
JOURNAL OF BIOMEDICAL MATERIALS RESEARCH PART A, 2003, 64A (01) :70-79
[3]   Photopolymerization kinetics of methacrylate dental resins [J].
Dickens, SH ;
Stansbury, JW ;
Choi, KM ;
Floyd, CJE .
MACROMOLECULES, 2003, 36 (16) :6043-6053
[4]  
Drumright RE, 2000, ADV MATER, V12, P1841, DOI 10.1002/1521-4095(200012)12:23<1841::AID-ADMA1841>3.0.CO
[5]  
2-E
[6]   Transdermal photopolymerization for minimally invasive implantation [J].
Elisseeff, J ;
Anseth, K ;
Sims, D ;
McIntosh, W ;
Randolph, M ;
Langer, R .
PROCEEDINGS OF THE NATIONAL ACADEMY OF SCIENCES OF THE UNITED STATES OF AMERICA, 1999, 96 (06) :3104-3107
[7]  
Fox TG., 1956, Bulletin of the American Physical Society, V1, P123
[8]   IDEAL COPOLYMERS AND THE 2ND-ORDER TRANSITIONS OF SYNTHETIC RUBBERS .1. NON-CRYSTALLINE COPOLYMERS [J].
GORDON, M ;
TAYLOR, JS .
JOURNAL OF APPLIED CHEMISTRY, 1952, 2 (09) :493-500
[9]   Synthesis of polymer network scaffolds from L-lactide and poly(ethylene glycol) and their interaction with cells [J].
Han, DK ;
Hubbell, JA .
MACROMOLECULES, 1997, 30 (20) :6077-6083
[10]   Injectable biodegradable polymer composites based on poly(propylene fumarate) crosslinked with poly(ethylene glycol)-dimethacrylate [J].
He, SL ;
Yaszemski, MJ ;
Yasko, AW ;
Engel, PS ;
Mikos, AG .
BIOMATERIALS, 2000, 21 (23) :2389-2394