The influence of crystalline and aggregate structure on PTC characteristic of conductive polyethylene carbon black composite

被引：108

作者：

Luo, YL ^{[1
]}

Wang, GC ^{[1
]}

Zhang, BY ^{[1
]}

Zhang, ZP ^{[1
]}

机构：

[1] E China Univ Chem Technol, Inst Mat Sci & Engn, Shanghai 200237, Peoples R China

来源：

EUROPEAN POLYMER JOURNAL | 1998年 / 34卷 / 08期

关键词：

D O I：

10.1016/S0014-3057(98)00099-8

中图分类号：

O63 [高分子化学（高聚物）];

学科分类号：

070305 ; 080501 ; 081704 ;

摘要：

The relationship between conductivity and morphological structure of a polyethylene/carbon black composite (PE/CB) was investigated by DSC, WAXD and SAXS, and a new interpretation of the PTC (positive temperature coefficient) effect has been proposed. The PTC intensity enhanced:with increased crystallinity for the PE/CB system; a substantial PTC effect was not discovered in an amorphous polymer/CB system. The behaviour of melting, crystallization and aggregate "large size" properties of the polymer matrix were modified by annealing, which in turn made the PTC intensity increase. It is pointed out that not only crystallinity, but also long spacing and lamellar size, also affect the PTC performances. (C) 1998 Elsevier Science Ltd. All rights reserved.

引用

页码：1221 / 1227

页数：7

共 20 条

[1]

Brundrup J., 1989, POLYM HDB

[2] STRUCTURE AND ORIENTATION IN THIN FILMS OF POLYTHENE [J].

CHARLESBY, A .

PROCEEDINGS OF THE PHYSICAL SOCIETY OF LONDON, 1945, 57 (324) :496-&

[3]

Fred K., 1966, US patent, Patent No. 3243753

[4]

HUANG XM, 1992, WIRE CABLE, V4, P7

[5]

ISHIBASHI M, 1988, FUJIKURA TECHNICAL R, V17, P51

[6]

KAKUDO M, 1972, XRAY DIFFRACTION POL, P821

[7]

LEE M, 1983, Patent No. 4413301

[8] PROPERTIES AND STRUCTURES OF FILMS DRAWN FROM POLYETHYLENE SINGLE-CRYSTAL MATS [J].

MAEDA, M ;

MIYASAKA, K ;

ISHIKAWA, K .

JOURNAL OF POLYMER SCIENCE PART A-2-POLYMER PHYSICS, 1970, 8 (03) :355-&

[9] GLASS TRANSITION TEMPERATURE AS A GUIDE TO SELECTION OF POLYMERS SUITABLE FOR PTC MATERIALS [J].

MEYER, J .

POLYMER ENGINEERING AND SCIENCE, 1973, 13 (06) :462-468

[10]

MO ZS, 1981, SYNTHETIC FIBERS, V5, P65

← 1 2 →