Co/Pd and Co/Pt multilayers with indium tin oxide seed layers and NiFe soft underlayers for perpendicular magnetic recording media

Co/Pd and Co/Pt multilayers have been fabricated on ultra-thin (2 nm) indium tin oxide (ITO) seed layers with soft underlayer for perpendicular magnetic recording. The coercivity of the Co/Pd multilayers was increased from 5.1 kOe to 6.3 kOe by increasing the thickness of the initial I'd layer from 1 mn to 2 nm. Hysteresis loops with an almost perfect remanent squareness, high nucleation field, and more sheared sides were obtained. TEM analysis shows that the films have well-segregated columnar structures which help to reduce exchange coupling and increase coercivity. Spin-stand testing shows that the Co/Pd multilayers have a D50 about 157 kfci without differentiating the output signals. Co/pt multilayers with ITO seed layers deposited in 40 mTorr of Kr give a coercivity of 6.9 kOe and a D50 about 290 kfci when the output signal is differentiated.