Improving glass forming ability of Zr50.5Cu36.5Ni4Al9 alloy by suppressing CuZr phase precipitation

被引：16

作者：

Deng, S. T. ^{[1
,2
]}

Zhang, H. F. ^{[1
]}

Wang, A. M. ^{[1
]}

Li, H. ^{[1
]}

Ding, B. Z. ^{[1
]}

Hu, Z. Q. ^{[1
]}

机构：

[1] Chinese Acad Sci, Met Res Inst, Shenyang Natl Lab Mat Sci, Shenyang 110016, Peoples R China

[2] Chinese Acad Sci, Grad Sch, Beijing 100039, Peoples R China

来源：

JOURNAL OF ALLOYS AND COMPOUNDS | 2008年 / 460卷 / 1-2期

基金：

中国国家自然科学基金;

关键词：

amorphous materials; amorphisation;

D O I：

10.1016/j.jallcom.2007.05.062

中图分类号：

O64 [物理化学（理论化学）、化学物理学];

学科分类号：

070304 ; 081704 ;

摘要：

CuZr phase is precipitated easily in the process of fabricating Zr50.5Cu34.5Ni4Al11 BMG. The critical diameter of amorphous rod is improved from 8 mm of Zr50.5Cu34.5Ni4Al11 to at least 20 mm of Zr53.5Cu26.5Ni5Al12Ag3 by restraining the precipitation of CuZr phase. The great improvement of GFA is attributed to the declination of Cu content and the weakening of the drastic interaction between Cu and Zr atoms by Ag addition since Ag has similarly physical and chemical properties with Cu. Therefore, suppressing the precipitation of crystalline phase should be an effective method to enhance GFA. (C) 2007 Elsevier B.V. All rights reserved.

引用

页码：182 / 185

页数：4

共 16 条

[1]

ATAKAN P, 1994, THESIS CALTECH

[2]

CHAMBERS C, 1975, MOD INORG CHEM, P1

[3] COMPOSITION REQUIREMENTS FOR GLASS FORMATION IN METALLIC AND IONIC SYSTEMS [J].

COHEN, MH ;

TURNBULL, D .

NATURE, 1961, 189 (475) :131-&

[4]

DEBOER FR, 1988, COHENSION METALS

[5] Zr-Cu-Ni-Al-Ta glassy matrix composites with enhanced plasticity [J].

Dong, Wenbo ;

Zhang, Haifeng ;

Sun, Wensheng ;

Wang, Aimin ;

Li, Hong ;

Hu, Zhuangqi .

JOURNAL OF MATERIALS RESEARCH, 2006, 21 (06) :1490-1499

[6] MATERIALS SCIENCE - CONFUSION BY DESIGN [J].

GREER, AL .

NATURE, 1993, 366 (6453) :303-304

[7] Stabilization of metallic supercooled liquid and bulk amorphous alloys [J].

Inoue, A .

ACTA MATERIALIA, 2000, 48 (01) :279-306

[8] Effect of additional elements on glass transition behavior and glass formation tendency of Zr-Al-Cu-Ni alloys [J].

Inoue, A ;

Shibata, T ;

Zhang, T .

MATERIALS TRANSACTIONS JIM, 1995, 36 (12) :1420-1426

[9]

LIN XH, 1997, THESIS CALTECH, P16

[10] Glass formation criterion for various glass-forming systems [J].

Lu, ZP ;

Liu, CT .

PHYSICAL REVIEW LETTERS, 2003, 91 (11)

← 1 2 →