Evaluation of compatibility of EPDM and butyl rubber - II. Thermal and radiation stability

被引：18

作者：

Zaharescu, T

Jipa, S

Giurginca, M

Podina, C

机构：

[1] R&D Inst Elect Engn, Bucharest 74204, Romania

[2] CERELAST, Bucharest 79628, Romania

[3] Univ Bucharest, Fac Chem, Bucharest 70346, Romania

来源：

POLYMER DEGRADATION AND STABILITY | 1998年 / 62卷 / 03期

关键词：

D O I：

10.1016/S0141-3910(98)00043-3

中图分类号：

O63 [高分子化学（高聚物）];

学科分类号：

070305 ; 080501 ; 081704 ;

摘要：

The exposure of ethylene-propylene terpolymer/butyl rubber blends to gamma radiation was carried out in order to evaluate the level of their compatibilization. Three concentrations of the components (3:1, 1:1 and 1:3) were prepared. Gel content measurements were performed in o-xylene and oxygen uptake was used to characterize the oxidation stability of irradiated specimens. The optimal dose range for efficient crosslinking of EPDM/IIR blends is around 200 kGy. The derivatives of the [O-2] = f(t) dependences indicate the order of thermal stability of radiochemically processed samples. (C) 1998 Elsevier Science Limited. All rights reserved.

引用

页码：569 / 574

页数：6

共 18 条

[1] KINETIC STUDIES IN THE CHEMISTRY OF RUBBER AND RELATED MATERIALS .2. THE KINETICS OF OXIDATION OF UNCONJUGATED OLEFINS [J].

BOLLAND, JL ;

GEE, G .

TRANSACTIONS OF THE FARADAY SOCIETY, 1946, 42 (3-4) :236-243

[2]

CARLSSON DJ, 1986, ENCY POLYM SCI ENG, V4, P630

[3]

DEURI AS, 1992, POLYM DEGRAD STABIL, V38, P173

[4] TIME TEMPERATURE DOSE-RATE SUPERPOSITION - A METHODOLOGY FOR EXTRAPOLATING ACCELERATED RADIATION AGING DATA TO LOW-DOSE RATE CONDITIONS [J].

GILLEN, KT ;

CLOUGH, RL .

POLYMER DEGRADATION AND STABILITY, 1989, 24 (02) :137-168

[5] Thermo-oxidative behaviour of halobutyl and butyl elastomers [J].

Jipa, S ;

Giurginca, M ;

Setnescu, T ;

Setnescu, R ;

Ivan, G ;

Mihalcea, I .

POLYMER DEGRADATION AND STABILITY, 1996, 54 (01) :1-6

[6]

MIHALCEA I, 1982, MAT PLASTICE BUCHARE, V19, P170

[7]

NANDO GB, 1988, PLAST RUB PROC APPL, V9, P29

[8]

SAUNDERS CB, 1988, AECL9569

[9]

SCOTT G, 1977, DEV POLYM DEGRADATIO, V1, pCH7

[10]

VANGISBERGEN JGM, 1991, THESIS TU EINDHOVEN

← 1 2 →