Aligned SnS2 nanotubes fabricated via a template-assisted solvent-relief process

被引：35

作者：

Chen, D

Shen, GZ

Tang, KB ^{[1
]}

Liu, YK

Qian, YT

机构：

[1] Univ Sci & Technol China, Dept Chem, Hefei 230026, Anhui, Peoples R China

[2] Univ Sci & Technol China, Struct Res Lab, Hefei 230026, Anhui, Peoples R China

来源：

APPLIED PHYSICS A-MATERIALS SCIENCE & PROCESSING | 2003年 / 77卷 / 06期

关键词：

D O I：

10.1007/s00339-003-2215-4

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

The template-assisted solvent-relief (TASR) process was applied to prepare aligned tin disulfide nanotubes, using SnCl4 and thiourea as the raw materials at 140 degreesC for 15 h in an alcohol solution. The product was characterized by X-ray powder diffraction (XRD) and transmission electron microscopy (TEM). The XRD pattern showed that the sample was hexagonal-phase SnS2 with a preferred orientation. The TEM observations indicate that the as-synthesized SnS2 nanotubes that were produced were of high quality and uniform size.

引用

收藏

页码：747 / 749

页数：3

相关论文

共 19 条

[1] Design and self-assembly of open, regular, 3D mesostructures [J].

Breen, TL ;

Tien, J ;

Oliver, SRJ ;

Hadzic, T ;

Whitesides, GM .

SCIENCE, 1999, 284 (5416) :948-951

[2] ANODIC OXIDE FILMS ON ALUMINUM [J].

DIGGLE, JW ;

DOWNIE, TC ;

GOULDING, CW .

CHEMICAL REVIEWS, 1969, 69 (03) :365-&

[3] Preparation and photoluminescence of alumina membranes with ordered pore arrays [J].

Du, Y ;

Cai, WL ;

Mo, CM ;

Chen, J ;

Zhang, LD ;

Zhu, XG .

APPLIED PHYSICS LETTERS, 1999, 74 (20) :2951-2953

[4] Synthesis of SnS2 nanocrystals via a solvothermal process [J].

Hai, B ;

Tang, KB ;

Wang, CR ;

An, CH ;

Yang, Q ;

Shen, GZ ;

Qian, YT .

JOURNAL OF CRYSTAL GROWTH, 2001, 225 (01) :92-95

[5] Hydrothermal growth of β-Ag2Se tubular crystals [J].

Hu, JQ ;

Deng, B ;

Lu, QY ;

Tang, KB ;

Jiang, RR ;

Qian, YT ;

Zhou, GE ;

Cheng, A .

CHEMICAL COMMUNICATIONS, 2000, (08) :715-716

[6] HELICAL MICROTUBULES OF GRAPHITIC CARBON [J].

IIJIMA, S .

NATURE, 1991, 354 (6348) :56-58

[7] A catalytic-assembly solvothermal route to multiwall carbon nanotubes at a moderate temperature [J].

Jiang, Y ;

Wu, Y ;

Zhang, SY ;

Xu, CY ;

Yu, WC ;

Xie, Y ;

Qian, YT .

JOURNAL OF THE AMERICAN CHEMICAL SOCIETY, 2000, 122 (49) :12383-12384

[8]

Kasuga T, 1999, ADV MATER, V11, P1307, DOI 10.1002/(SICI)1521-4095(199910)11:15<1307::AID-ADMA1307>3.0.CO

[9]

2-H

[10] Morphology and topochemical reactions of novel vanadium oxide nanotubes [J].

Krumeich, F ;

Muhr, HJ ;

Niederberger, M ;

Bieri, F ;

Schnyder, B ;

Nesper, R .

JOURNAL OF THE AMERICAN CHEMICAL SOCIETY, 1999, 121 (36) :8324-8331