Hydrothermal synthesis and phase stability of new zircon- and scheelite-type ZrGeO4

被引:46
作者
Hirano, M [1 ]
Morikawa, H [1 ]
机构
[1] Aichi Inst Technol, Fac Engn, Dept Appl Chem, Toyota 4700392, Japan
关键词
D O I
10.1021/cm020661q
中图分类号
O64 [物理化学(理论化学)、化学物理学];
学科分类号
070304 ; 081704 ;
摘要
Single-phase zircon- and sheelite-type ZrGeO4 were selectively synthesized from the reaction of a ZrOCl2 solution and GeO2 under mild hydrothermal conditions at 120-240 degreesC by PH control of the solution via homogeneous generation of a hydroxide ion through the decomposition of urea. New phase zircon-type ZrGeO4 octahedral-like particles that were assemblies of small crystals (10-80 nm in size) were directly formed under acid conditions, and the particle size was controlled (0.4-1.5 mum in size) by the absence or presence of urea as well as hydrothermal treatment temperature. Scheelite-type ZrGeO4 particles (50-100 nm in size) that were a coagulation of nanometer-sized crystals were formed under moderate neutral to acid conditions (6 greater than or equal to PH > 2) in the presence of urea. The zircon-type ZrGeO4 was stable below 1160 degreesC in air and transformed to the scheelite-type structure at 1180 degreesC. The dissociation of ZrGeO4 to tetragonal ZrO2 and GeO2 occurred by heat treatment under conditions above 1350 degreesC for 5 h or 1450 degreesC for 1 h.
引用
收藏
页码:2561 / 2566
页数:6
相关论文
共 29 条
[1]  
BERTAUT F, 1954, CR HEBD ACAD SCI, V238, P2173
[2]   THE FLUX GROWTH OF SINGLE-CRYSTALS OF VANADIUM-DOPED ZRSIO4, HFSIO4, ZRGEO4 AND HFGEO4 AS WELL AS OF CHROMIUM-DOPED ZRSIO4 AND TERBIUM-DOPED ZRGEO4 [J].
CHANDLEY, P ;
CLARK, RJH .
JOURNAL OF CRYSTAL GROWTH, 1992, 116 (1-2) :151-157
[3]   THE CRYSTAL STRUCTURE OF ZIRCONYL CHLORIDE OCTAHYDRATE AND ZIRCONYL BROMIDE OCTAHYDRATE [J].
CLEARFIELD, A ;
VAUGHAN, PA .
ACTA CRYSTALLOGRAPHICA, 1956, 9 (06) :555-558
[4]   INVESTIGATION OF THE THERMAL DISSOCIATION, REASSOCIATION, AND SYNTHESIS OF ZIRCON [J].
CURTIS, CE ;
SOWMAN, HG .
JOURNAL OF THE AMERICAN CERAMIC SOCIETY, 1953, 36 (06) :190-198
[5]   NEUTRON-DIFFRACTION DETERMINATION OF THE STRUCTURE OF AN ORDERED SCHEELITE-TYPE - ZR3GEO8 [J].
ENNACIRI, A ;
MICHEL, D ;
JORBA, MPY .
MATERIALS RESEARCH BULLETIN, 1984, 19 (06) :793-799
[6]   CRYSTAL-STRUCTURES OF HFGEO4 AND THGEO4 GERMANATES [J].
ENNACIRI, A ;
KAHN, A ;
MICHEL, D .
JOURNAL OF THE LESS-COMMON METALS, 1986, 124 :105-109
[7]  
Hirano M, 2000, J AM CERAM SOC, V83, P1287
[8]   Preparation of monodispersed cerium(IV) oxide particles by thermal hydrolysis: influence of the presence of urea and Gd doping on their morphology and growth [J].
Hirano, M ;
Inagaki, M .
JOURNAL OF MATERIALS CHEMISTRY, 2000, 10 (02) :473-477
[9]   Hydrothermal synthesis and characterization of ZnGa2O4 spinel fine particles [J].
Hirano, M .
JOURNAL OF MATERIALS CHEMISTRY, 2000, 10 (02) :469-472
[10]   Direct synthesis of new zircon-type ZrGeO4 and Zr(Ge,Si)O4 solid solutions [J].
Hirano, M ;
Morikawa, H ;
Inagaki, M ;
Toyoda, M .
JOURNAL OF THE AMERICAN CERAMIC SOCIETY, 2002, 85 (08) :1915-1920