High voltage silicon carbide devices

Progress made in the development of high performance power rectifiers and switches from silicon carbide are reviewed with emphasis on approaching the 100-fold reduction in the specific an-resistance of the drift region when compared with silicon devices with the same breakdown voltage. The highlights are: (a) Recently completed measurements of impact ionization coefficients in SiC indicate an even higher Baliga's figure of merit than projected earlier. (b) The commonly reported negative temperature co-efficient for breakdown voltage in SiC devices has been shown to arise at defects, allaying concerns that this may be intrinsic to the material. (c) Based upon fundamental considerations, it has been found that Schottky rectifiers offer superior on-state voltage drop than P-i-N rectifiers for reverse blocking voltages below 3000 volts. (d) Nearly ideal breakdown voltage has been experimentally obtained for Schottky diodes using an argon implanted edge termination. (e) Planar ion-implanted junctions have been successfully fabricated using oxide as a mask with high breakdown voltage and low leakage currents by using a filed plate edge termination. (f) High inversion layer mobility has been experimentally demonstrated on both 6H and 4H-SiC by using a deposited oxide layer as gate dielectric. (g) A novel, high-voltage, normally-off, accumulation-channel, MOSFET has been proposed and demonstrated with 50x lower specific on-resistance than silicon devices in spite of using logic-level gate drive voltages. These results indicate that SiC based power devices could become commercially viable in the 21st century if cost barriers can be overcome.