Martensitic transformations in NiMnAl beta phase alloys

被引：89

作者：

Kainuma, R ^{[1
]}

Nakano, H ^{[1
]}

Ishida, K ^{[1
]}

机构：

[1] HITACHI MET CO,MOKA 32143,JAPAN

来源：

METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE | 1996年 / 27卷 / 12期

关键词：

D O I：

10.1007/BF02595663

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

Martensitic transformation characteristics in a wide range of alloy compositions in the NiMnAl system have been investigated by differential scanning calorimetry (DSC), X-ray diffraction (XRD), and transmission electron microscopy (TEM)I The results indicate that while the NiMnAl alloys with relatively high Al and Mn contents transform martensitically to either the 14M(7R) or the 10M phase with a long-period stacking-order structure, those with low Al or Mn contents transform to the L1(0)(3R:2M) structure. The M(s) temperature and the cia ratio of the L1(0) martensite increase with decreasing Al or Mn content. In the Ni-30Mn-20Al alloy, typical premartensite microstructures, such as needlelike, modulated, and tweed structures, are observed and it is also found that a distorted B2 structure is formed as an intermediate phase prior to transformation to the 10M martensite.

引用

页码：4153 / 4162

页数：10

共 28 条

[1] TRANSFORMATION BEHAVIOR OF NEARLY STOICHIOMETRIC NI-MN ALLOYS [J].

ADACHI, K ;

WAYMAN, CM .

METALLURGICAL TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1985, 16 (09) :1567-1579

[2]

[Anonymous], BINARY ALLOY PHASE D

[3] CRYSTAL-STRUCTURE AND INTERNAL TWINS OF NI-36.8 AT PERCENT A1 MARTENSITE [J].

ENAMI, K ;

NENNO, S ;

SHIMIZU, K .

TRANSACTIONS OF THE JAPAN INSTITUTE OF METALS, 1973, 14 (02) :161-165

[4]

ENAMI K, 1971, METALL TRANS, V2, P1487

[5]

HORTON JA, 1995, MATER RES SOC SYMP P, V360, P549

[6] NEW MARTENSITE STRUCTURES AND COMPOSITION DEPENDENCE OF MARTENSITIC TRANSFORMATIONS IN NI50ALXMN50-X ALLOYS [J].

INOUE, T ;

MORITO, S ;

MURAKAMI, Y ;

ODA, K ;

OTSUKA, K .

MATERIALS LETTERS, 1994, 19 (1-2) :33-37

[7] DUCTILITY ENHANCEMENT IN NIAL (B2)-BASE ALLOYS BY MICROSTRUCTURAL CONTROL [J].

ISHIDA, K ;

KAINUMA, R ;

UENO, N ;

NISHIZAWA, T .

METALLURGICAL TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1991, 22 (02) :441-446

[8]

Ishida K., 1995, Mechanical Properties and Phase Transformations of Multiphase Intermetallic Alloys. Proceedings of a Symposium, P77

[9]

KAINUMA R, 1992, MATER RES SOC SYMP P, V246, P403

[10]

KAINUMA R, 1995, MATER RES SOC SYMP P, V360, P467

← 1 2 3 →