Identification of hot corrosion resistant MCrAlY based bond coatings for gas turbine engine applications

被引：118

作者：

Gurrappa, I ^{[1
]}

机构：

[1] Def Met Res Lab, Hyderabad 500058, Andhra Pradesh, India

来源：

SURFACE & COATINGS TECHNOLOGY | 2001年 / 139卷 / 2-3期

关键词：

MCrAlY coatings; hot corrosion; gas turbines; electrochemical mechanism;

D O I：

10.1016/S0257-8972(00)01156-7

中图分类号：

TB3 [工程材料学];

学科分类号：

0805 ; 080502 ;

摘要：

In the current paper, an attempt has been made to identify hot corrosion resistant coatings which can produce a thermodynamically stable and inert oxide scale during exposure to a hot corrosion environment and thereby enhance the coating life significantly. The results obtained from hot corrosion tests of a variety of MCrAlY-type coatings with different alloying elements and traces of silicon and hafnium in the presence of sodium chloride and vanadium containing environments revealed that a NiCoCrAlY coating exhibits maximum life time among the coatings studied. The results also revealed that presence of trace elements in the coating reduces coating life significantly. Based on the results, a novel electrochemical mechanism has been proposed. It has been shown that the hot corrosion of protective coatings is an electrochemical phenomena and hence the electrochemical techniques appear to be quite useful in evaluating coatings for hot corrosion resistance. (C) 2001 Elsevier Science B.V. All rights reserved.

引用

页码：272 / 283

页数：12

共 17 条

[1] Long-term oxidation tests on a Re-containing MCrAlY coating [J].

Beele, W ;

Czech, N ;

Quadakkers, WJ ;

Stamm, W .

SURFACE & COATINGS TECHNOLOGY, 1997, 94-5 (1-3) :41-45

[2] The oxidation behaviour of sprayed MCrAlY coatings [J].

Brandl, W ;

Grabke, HJ ;

Toma, D ;

Kruger, J .

SURFACE & COATINGS TECHNOLOGY, 1996, 86 (1-3) :41-47

[3]

CONDE JFG, 1982, P C HIGH TEMPERATURE, P237

[4]

DESAI V, 1997, P INT C CORR CONCORR, P216

[5] DEVELOPMENT OF A LOW-EXPANSION BOND COATING FOR NI-BASE SUPERALLOYS [J].

FRITSCHER, K ;

LEYENS, C ;

PETERS, M .

MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 1995, 190 (1-2) :253-258

[6]

GOEBEL JA, 1981, P 2 C ADV MAT ALT FU

[7]

GOWARD GW, 1986, J MATER SCI TECHNOL, V2, P197

[8]

GRISIK JJ, 1980, P INT C MET COAT SAN, P397

[9] Hot corrosion behavior of CM 247 LC alloy in Na2SO4 and NaCl environments [J].

Gurrappa, I .

OXIDATION OF METALS, 1999, 51 (5-6) :353-382

[10]

GURRAPPA I, 1999, J ELECTROCHEM SOC, V48, P187

← 1 2 →