Preparation of monodispersed cubic calcium carbonate particles via precipitation reaction

被引:114
作者
Cheng, B
Lei, M
Yu, JG
Zhao, XJ
机构
[1] Wuhan Univ Technol, State Key Lab Adv Technol Mat Synth & Proc, Wuhan 430070, Peoples R China
[2] Wuhan Univ Technol, Minist Educ, Key Lab Silicate Mat & Engn, Wuhan 430070, Peoples R China
基金
中国国家自然科学基金;
关键词
CaCO3; preparation; polyacrylic acid (PAA); temperature; cubic; monodispersed; composite;
D O I
10.1016/j.matlet.2003.10.027
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
Monodispersed cubic calcium carbonate composite particles were prepared by the precipitation reaction of sodium carbonate with calcium chloride in water in the presence of polyacrylic acid (PAA) at 60-80 degreesC, and then characterized with scanning electron microscopy (SEM), X-ray diffraction (XRD) and Differential Scanning Calorimetry-Thermogravimetry (DSC-TG). It was found from the above results that variations in the concentration of PAA and CaCO3, molar ratio of PAA to CaCO3, and pH and temperature of solution drastically changed the morphology of the as-produced CaCO3 particles, but all the products obtained consisted of calcite crystals. The optimal experimental conditions for the production of cubic calcite particles were determined. The amount of PAA in the cubic calcite composite particles was about 1.4%. (C) 2003 Elsevier B.V. All rights reserved.
引用
收藏
页码:1565 / 1570
页数:6
相关论文
共 13 条
[1]   Shape-controlled synthesis of colloidal platinum nanoparticles [J].
Ahmadi, TS ;
Wang, ZL ;
Green, TC ;
Henglein, A ;
ElSayed, MA .
SCIENCE, 1996, 272 (5270) :1924-1926
[2]  
[Anonymous], 1995, BIOMIMETIC MAT CHEM
[3]  
Cölfen H, 2001, CHEM-EUR J, V7, P106
[4]   The overgrowth of calcium carbonate on poly(vinyl chloride-co-vinyl acetate-co-maleic acid) [J].
Dalas, E ;
Klepetsanis, P ;
Koutsoukos, PG .
LANGMUIR, 1999, 15 (23) :8322-8327
[5]   Control of calcite crystal morphology by a peptide designed to bind to a specific surface [J].
DeOliveira, DB ;
Laursen, RA .
JOURNAL OF THE AMERICAN CHEMICAL SOCIETY, 1997, 119 (44) :10627-10631
[6]   Control of aragonite or calcite polymorphism by mollusk shell macromolecules [J].
Falini, G ;
Albeck, S ;
Weiner, S ;
Addadi, L .
SCIENCE, 1996, 271 (5245) :67-69
[7]   MOLECULAR TECTONICS IN BIOMINERALIZATION AND BIOMIMETIC MATERIALS CHEMISTRY [J].
MANN, S .
NATURE, 1993, 365 (6446) :499-505
[8]   Synthesis of inorganic materials with complex form [J].
Mann, S ;
Ozin, GA .
NATURE, 1996, 382 (6589) :313-318
[9]  
Mann S, 1989, BIOMINERALIZATION CH
[10]   Controlled colloid formation [J].
Matijevic, E .
CURRENT OPINION IN COLLOID & INTERFACE SCIENCE, 1996, 1 (02) :176-183